PA6 Durethan® BKV315ZH2.0 901510 LANXESS GERMANY

350

Unit Price:US$ 3,060 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
45.5MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	65	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	70	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	85	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
BurningBehavior		ISO 3795	passed
UL flame retardant rating	3.2mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.6mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	3.5%Strain	ISO 178/A	150	Mpa
Bending modulus	23°C	ISO 178/A	4800	Mpa
Tensile strain	Break,23°C	ISO 527-2/5	5.0	%
tensile strength	Break,23°C	ISO 527-2/5	105	Mpa
Tensile modulus	23°C	ISO 527-2/1	5300	Mpa
bending strength	23°C	ISO 178	165	Mpa
bending strength	bending strength	FlexuralStrainatFlexuralStrength5(23°C)		5.5	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	1.3E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	4E-05	cm/cm/°C
Melting temperature		ISO 11357-3	221	°C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	58.0	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	175	°C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	210	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD:120°C,2hr,2.00mm3	ISO 294-4	0.20	%
	Shrinkage rate	MD:280°C,2.00mm2	ISO 294-4	0.90	%
		Shrinkage rate	TD:120°C,2hr,2.00mm3	ISO 294-4	0.10	%
		Shrinkage rate	Shrinkage rate	TD:280°C,2.00mm2	ISO 294-4	0.60	%
Apparent density		ISO 60	0.70	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 2
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	140	Mpa
film	Test Condition	Test Method	Test Result	Test Unit
Thin film puncture strength	--6	ISO 6603-2	2.50	J
	Thin film puncture strength	--7	ISO 6603-2	4.90	J
		Thin film puncture strength	--6	ISO 6603-2	630	N
		Thin film puncture strength	Thin film puncture strength	--7	ISO 6603-2	1200	N
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ISO Shortcut		ISO 1874	PA6-HI.BHR.14-050.GF15

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA6 Durethan® BKV315ZH2.0 901510 LANXESS GERMANY

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index