PA6 BKV315ZH2.0 901510 LANXESS GERMANY
Durethan®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LANXESS GERMANY/BKV315ZH2.0 901510 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 70 kJ/m² |
| 23°C | ISO 180/1U | 65 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 80 kJ/m² |
| -30°C | ISO 179/1eU | 85 kJ/m² |
| hardness | Test Condition | Test Method | LANXESS GERMANY/BKV315ZH2.0 901510 |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 140 Mpa |
| Supplementary Information | Test Condition | Test Method | LANXESS GERMANY/BKV315ZH2.0 901510 |
|---|---|---|---|
| ISO Shortcut | ISO 1874 | PA6-HI.BHR.14-050.GF15 |
| film | Test Condition | Test Method | LANXESS GERMANY/BKV315ZH2.0 901510 |
|---|---|---|---|
| Thin film puncture strength | --7 | ISO 6603-2 | 4.90 J |
| --6 | ISO 6603-2 | 630 N | |
| --7 | ISO 6603-2 | 1200 N | |
| --6 | ISO 6603-2 | 2.50 J |
| Electrical performance | Test Condition | Test Method | LANXESS GERMANY/BKV315ZH2.0 901510 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| Mechanical properties | Test Condition | Test Method | LANXESS GERMANY/BKV315ZH2.0 901510 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 5.0 % |
| Flexural modulus | 23°C | ISO 178/A | 4800 Mpa |
| bending strength | 3.5%Strain | ISO 178/A | 150 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 105 Mpa |
| bending strength | 23°C | ISO 178 | 165 Mpa |
| Tensile modulus | 23°C | ISO 527-2/1 | 5300 Mpa |
| bending strength | FlexuralStrainatFlexuralStrength5(23°C) | 5.5 % |
| flammability | Test Condition | Test Method | LANXESS GERMANY/BKV315ZH2.0 901510 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| 1.6mm | UL 94 | HB | |
| Burning Behavior | ISO 3795 | passed |
| physical property | Test Condition | Test Method | LANXESS GERMANY/BKV315ZH2.0 901510 |
|---|---|---|---|
| Shrinkage rate | TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.10 % |
| Apparent density | ISO 60 | 0.70 g/cm³ | |
| Shrinkage rate | TD:280°C,2.00mm2 | ISO 294-4 | 0.60 % |
| MD:280°C,2.00mm2 | ISO 294-4 | 0.90 % | |
| MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.20 % |
| Thermal performance | Test Condition | Test Method | LANXESS GERMANY/BKV315ZH2.0 901510 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 221 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 4E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 210 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 1.3E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 175 °C |
| 8.0MPa,未退火，HDT | ISO 75-2/C | 58.0 °C |