PPO NORYL™ HS2000X-80267 SABIC INNOVATIVE THAILAND
199
- Unit Price:US$ 4,529 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber mineral reinforcement
- Application Areas:medical care
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 7.6 g/10min | |
| ASTM D1238 | 7.6 g/10min | ||
| Melt volume flow rate | ISO 1133 | 6.80 cm3/10min | |
| ISO 1133 | 6.80 cm3/10min | ||
| Shrinkage rate | 内部方法 | 0.50-0.70 % | |
| Outdoor applicability | UL 746C | f1 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| UL 94 | 5VA | ||
| UL 94 | YES |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| --1 | ASTM D638 | 3650 Mpa | |
| yield | ASTM D638 | 74.0 Mpa | |
| Yield, 100mm span | ASTM D790 | 117 Mpa | |
| Fracture, 50.0mm span | ASTM D790 | 117 Mpa | |
| yield | ISO 527-2 | 71.7 Mpa | |
| fracture | ASTM D638 | 60.0 Mpa | |
| ISO 527-2 | 57.1 Mpa | ||
| yield | ASTM D638 | 3.8 % | |
| ISO 527-2 | 3.7 % | ||
| fracture | ASTM D638 | 8.4 % | |
| ISO 527-2 | 11 % | ||
| 100mm span 5 | ASTM D790 | 3550 Mpa | |
| 50.0mm span | ASTM D790 | 3670 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 23°C | ASTM D256 | 130 J/m | |
| ISO 180/1A | 9.7 kJ/m² | ||
| Suspended wall beam without notch impact strength | ASTM D4812 | 2200 J/m | |
| Reverse notch impact | ASTM D256 | 810 J/m | |
| Dart impact | ASTM D3763 | 443 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | ASTM D150 | 4.4E-03 | |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
| High arc combustion index (HAI) | UL 746 | PLC 2 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 3 | |
| Hot wire ignition (HWI) | UL 746 | PLC 0 | |
| Surface Resistivity | ASTM D257 | >1.0E+16 ohms | |
| Volume resistivity | ASTM D257 | 1.2E+16 ohms·cm | |
| dielectric strength | ASTM D149 | 17 KV/mm | |
| dielectric constant | ASTM D150 | 2.89 | |
| ASTM D150 | 2.89 | ||
| ASTM D150 | 2.70 | ||
| Dissipation Factor | ASTM D150 | 0.017 | |
| ASTM D150 | 0.017 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 0.45MPa, Unanealed, 6.40mm | ASTM D648 | 128 °C | |
| 0.45MPa, Unanealed, 100mm span | ISO 75-2/Be | 126 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 108 °C | |
| 1.8MPa, Unanealed, 6.40mm | ASTM D648 | 116 °C | |
| 1.8MPa, Unanealed, 100mm span | ISO 75-2/Ae | 111 °C | |
| Linear coefficient of thermal expansion | ASTME831 | 7.1E-05 cm/cm/°C | |
| ASTME831 | 7.8E-05 cm/cm/°C | ||
| RTI Elec | UL 746 | 100 °C | |
| 0.45MPa, Unanealed, 3.20mm | ASTM D648 | 117 °C | |
| RTI Imp | UL 746 | 85.0 °C | |
| RTI | UL 746 | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.