Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO HS2000X-80267 SABIC INNOVATIVE THAILAND
NORYL™
medical care
Glass fiber mineral reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/HS2000X-80267 |
|---|---|---|---|
| 23°C | ISO 180/1A | 9.7 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 443 J |
| 23°C | ASTM D256 | 130 J/m | |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 2200 J/m |
| Reverse notch impact | 3.20mm | ASTM D256 | 810 J/m |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/HS2000X-80267 |
|---|---|---|---|
| Dissipation Factor | 50Hz | ASTM D150 | 0.017 |
| 60Hz | ASTM D150 | 0.017 | |
| dielectric constant | 60Hz | ASTM D150 | 2.89 |
| Volume resistivity | ASTM D257 | 1.2E+16 ohms·cm | |
| dielectric constant | 50Hz | ASTM D150 | 2.89 |
| Dissipation Factor | 1MHz | ASTM D150 | 4.4E-03 |
| Surface Resistivity | ASTM D257 | >1.0E+16 ohms | |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 2 |
| dielectric constant | 1MHz | ASTM D150 | 2.70 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| dielectric strength | 3.20mm,inOil | ASTM D149 | 17 KV/mm |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 0 |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/HS2000X-80267 |
|---|---|---|---|
| yield | ASTM D638 | 74.0 Mpa | |
| ASTM D638 | 3.8 % | ||
| fracture | ISO 527-2 | 11 % | |
| 100mm span 5 | 100mm | ASTM D790 | 3550 Mpa |
| fracture | ASTM D638 | 60.0 Mpa | |
| ISO 527-2 | 57.1 Mpa | ||
| yield | ISO 527-2 | 71.7 Mpa | |
| ISO 527-2 | 3.7 % | ||
| fracture | ASTM D638 | 8.4 % | |
| Yield, 100mm span | ASTM D790 | 117 Mpa | |
| 50.0mm span | ASTM D790 | 3670 Mpa | |
| --1 | ASTM D638 | 3650 Mpa | |
| Fracture, 50.0mm span | ASTM D790 | 117 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/HS2000X-80267 |
|---|---|---|---|
| UL flame retardant rating | 1.47mm | UL 94 | V-0 |
| RadiantPanelListing(UL) | UL 94 | YES | |
| 2.01mm | UL 94 | 5VA |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/HS2000X-80267 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 6.80 cm3/10min |
| melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 7.6 g/10min |
| Outdoor applicability | UL 746C | f1 | |
| melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 7.6 g/10min |
| Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 6.80 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/HS2000X-80267 |
|---|---|---|---|
| 0.45MPa, Unanealed, 6.40mm | ASTM D648 | 128 °C | |
| 0.45MPa, Unanealed, 100mm span | ISO 75-2/Be | 126 °C | |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 7.8E-05 cm/cm/°C |
| 1.8MPa, Unanealed, 100mm span | ISO 75-2/Ae | 111 °C | |
| RTI Imp | UL 746 | 85.0 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 108 °C | |
| 1.8MPa, Unanealed, 6.40mm | ASTM D648 | 116 °C | |
| RTI | UL 746 | 100 °C | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 7.1E-05 cm/cm/°C |
| RTI Elec | UL 746 | 100 °C | |
| 0.45MPa, Unanealed, 3.20mm | ASTM D648 | 117 °C |