PA6 LNP™ KONDUIT™ PX11311-WH9F059 SABIC INNOVATIVE US
4
- Unit Price:US$ 6,072 /MT
- Packaging Specification:
- Supply Quantity:20MT
- Delivery Terms:DDP
- :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Dimensional stability｜Low Specific Gravity
- Application Areas:Automotive body panels｜Automotive sector
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | ISO 1133 | 49.0 cm3/10min | |
| Shrinkage rate | ASTM D955 | 0.33 % | |
| ASTM D955 | 0.48 % | ||
| 23°C,24hr | 内部方法 | 0.25 % | |
| Balance, 23 ° C, 50% RH | ISO 62 | 0.040 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | IEC 60695-2-13 | 775 °C | |
| IEC 60695-2-13 | 850 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 7240 Mpa | |
| tensile strength | ASTM D638 | 52.0 Mpa | |
| elongation | ASTM D638 | 2.0 % | |
| Flexural modulus | ASTM D790 | 9050 Mpa | |
| bending strength | ASTM D790 | 76.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 5.3to18 kJ/m² | |
| Suspended wall beam without notch impact strength | ASTM D4812 | 180 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot wire ignition (HWI) | UL 746 | PLC 0 | |
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms | |
| dielectric strength | ASTM D149 | >10 KV/mm | |
| dielectric constant | ASTMES7-83 | 4.74 | |
| Dissipation Factor | ASTMES7-83 | 7.7E-03 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 199 °C | |
| Linear coefficient of thermal expansion | ASTME831 | 3.1E-05 cm/cm/°C | |
| ASTME831 | 1.9E-05 cm/cm/°C | ||
| ASTME831 | 4.6E-05 cm/cm/°C | ||
| ASTME831 | 7E-05 cm/cm/°C | ||
| specific heat | ASTMC351 | 1420 J/kg/°C | |
| --6 | ASTM D790/ISO 178 | 1.2 W/m/K | |
| --7 | ASTM D790/ISO 178 | 2.1 W/m/K | |
| --8 | ISO 22007-2 | 0.99 W/m/K | |
| --9 | ISO 22007-2 | 1.4 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.