PBT Toraycon® 5151G TORAY JAPAN
204
- Unit Price:US$ 3,491 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:32.8MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜High impact resistance
- Application Areas:Electrical applications｜Electrical components
- Color:--
- Grade:--
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M计秤,23°C | ISO 2039-2 | 70 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ASTM D-606 | 6.0 cm/cm×10 | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 185 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 95.0 °C | |
| Linear coefficient of thermal expansion | MD：-30到100°C | ISO 11359-2 | 9.5E-05 cm/cm/°C |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 105 ℃（℉） |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 6.0x10^-5 mm/mm.℃ |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 填充增强级.低翘曲 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 6.40 CM |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 45 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| arc resistance | ASTM D-495 | 110 秒 | |
| volume resistivity | ASTM D-257 | 1.5 cm/cm×10 | |
| dielectric strength | 短时·23℃·1/8时 | ASTM D-149 | 19 KV/mm |
| volume resistivity | IEC 60093 | 3E+16 ohms·cm | |
| dielectric strength | IEC 60243-1 | 19 KV/mm | |
| dielectric constant | 23°C,50Hz | IEC 60250 | 3.50 |
| 23°C,1kHz | IEC 60250 | 3.50 | |
| Dissipation Factor | 23°C,50Hz | IEC 60250 | 2E-03 |
| 23°C,1MHz | IEC 60250 | 0.020 | |
| arc resistance | IEC 60950 | 110 sec | |
| dielectric constant | ASTM D150/IEC 60250 | 3.5 | |
| volume resistivity | ASTM D257/IEC 60093 | 1.5x10^14 Ω.cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 80×80×3板材 | 1.4-1.9 % | |
| Water absorption rate | 23℃·24小时 | ASTM D-570 | 0.07 % |
| shrinkage rate | TD:3.00mm2 | 内部方法 | 1.9 % |
| MD:3.00mm4 | 内部方法 | 1.4 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.070 % |
| density | ASTM D792/ISO 1183 | 1.59 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.07 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 缺口，-40℃，1/8时宽 | ASTM D-256 | 3.0 kg.cm/cm |
| bending strength | 23℃ | ASTM D-790 | 930 kg/cm |
| flexural modulus | 23℃ | ASTM D-695 | 750 kg/cm |
| Elongation at break | 23℃ | ASTM D-638 | 6 % |
| flexural modulus | 23℃ | ASTM D-790 | 46 kg/cm |
| tensile strength | 23℃ | ASTM D-638 | 520 kg/cm |
| Heat Deflection Temperature | 4.6kg/cm | ASTM D-648 | 192 °C |
| 18.6kg.cm | ASTM D-648 | 85 °C | |
| Rockwell hardness | 23℃ | ASTM D-785 | 85 M标度 |
| coefficient of friction | 金属 | ASTM D-1894 | 0.14 |
| 本身 | ASTM D-1894 | 0.18 | |
| Impact strength of cantilever beam gap | 无缺口，23℃，1/8时宽 | ASTM D-256 | 50 kg.cm/cm |
| 无缺口，-40℃，1/8时宽 | ASTM D-256 | 30 kg.cm/cm | |
| 缺口，23℃，1/8时宽 | ASTM D-256 | 3.7 kg.cm/cm | |
| Tensile modulus | 23°C | ISO 527-2 | 5000 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 55.0 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 4.0 % |
| flexural modulus | 23°C | ISO 178 | 4500 Mpa |
| bending strength | 23°C | ISO 178 | 97.0 Mpa |
| coefficient of friction | 0.18 | ||
| Friction coefficient - vs. Metal | SuzukiMethod | 0.14 | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 35 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 30 kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 50 kg·cm/cm(J/M)ft·lb/in | ||
| Elongation at break | ASTM D638/ISO 527 | 5 % | |
| tensile strength | ASTM D638/ISO 527 | 55 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | M85 | |
| flexural modulus | ASTM D790/ISO 178 | 4200 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 90 kg/cm²(MPa)[Lb/in²] |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.