Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 5151G TORAY JAPAN
Toraycon®
Electrical applications,Electrical components
Flame retardant,High impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/5151G |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 45 kJ/m² |
| hardness | Test Condition | Test Method | TORAY JAPAN/5151G |
|---|---|---|---|
| Rockwell hardness | M计秤,23°C | ISO 2039-2 | 70 |
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/5151G |
|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 6.40 CM |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/5151G |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 50 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 90 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | 23℃ | ASTM D-785 | 85 M标度 |
| Flexural modulus | 23℃ | ASTM D-695 | 750 kg/cm |
| coefficient of friction | 本身 | ASTM D-1894 | 0.18 |
| Tensile modulus | 23°C | ISO 527-2 | 5000 Mpa |
| elongation at break | ASTM D638/ISO 527 | 5 % | |
| Rockwell hardness | ASTM D785 | M85 | |
| Impact strength of cantilever beam gap | 缺口，-40℃，1/8时宽 | ASTM D-256 | 3.0 kg.cm/cm |
| 缺口，23℃，1/8时宽 | ASTM D-256 | 3.7 kg.cm/cm | |
| Heat distortion temperature | 18.6kg.cm | ASTM D-648 | 85 °C |
| Flexural modulus | 23°C | ISO 178 | 4500 Mpa |
| coefficient of friction | 金属 | ASTM D-1894 | 0.14 |
| Flexural modulus | ASTM D790/ISO 178 | 4200 kg/cm²(MPa)[Lb/in²] | |
| coefficient of friction | 0.18 | ||
| Impact strength of cantilever beam gap | 无缺口，23℃，1/8时宽 | ASTM D-256 | 50 kg.cm/cm |
| tensile strength | ASTM D638/ISO 527 | 55 kg/cm²(MPa)[Lb/in²] | |
| Friction coefficient - vs. Metal | SuzukiMethod | 0.14 | |
| Heat distortion temperature | 4.6kg/cm | ASTM D-648 | 192 °C |
| Tensile strain | 断裂,23°C | ISO 527-2 | 4.0 % |
| bending strength | 23°C | ISO 178 | 97.0 Mpa |
| 23℃ | ASTM D-790 | 930 kg/cm | |
| elongation at break | 23℃ | ASTM D-638 | 6 % |
| tensile strength | 屈服,23°C | ISO 527-2 | 55.0 Mpa |
| Flexural modulus | 23℃ | ASTM D-790 | 46 kg/cm |
| tensile strength | 23℃ | ASTM D-638 | 520 kg/cm |
| Impact strength of cantilever beam gap | 无缺口，-40℃，1/8时宽 | ASTM D-256 | 30 kg.cm/cm |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/5151G |
|---|---|---|---|
| dielectric constant | 23°C,50Hz | IEC 60250 | 3.50 |
| 23°C,1kHz | IEC 60250 | 3.50 | |
| dielectric strength | IEC 60243-1 | 19 KV/mm | |
| Volume resistivity | IEC 60093 | 3E+16 ohms·cm | |
| arc resistance | IEC 60950 | 110 sec | |
| dielectric strength | 短时·23℃·1/8时 | ASTM D-149 | 19 KV/mm |
| dielectric constant | ASTM D150/IEC 60250 | 3.5 | |
| Dissipation Factor | 23°C,50Hz | IEC 60250 | 2E-03 |
| Volume resistivity | ASTM D-257 | 1.5 cm/cm×10 | |
| ASTM D257/IEC 60093 | 1.5x10^14 Ω.cm | ||
| arc resistance | ASTM D-495 | 110 秒 | |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 0.020 |
| other | Test Condition | Test Method | TORAY JAPAN/5151G |
|---|---|---|---|
| characteristic | 填充增强级.低翘曲 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/5151G |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.59 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.07 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/5151G |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY JAPAN/5151G |
|---|---|---|---|
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 1.9 % |
| MD:3.00mm4 | 内部方法 | 1.4 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.070 % |
| 23℃·24小时 | ASTM D-570 | 0.07 % | |
| Shrinkage rate | 80×80×3板材 | 1.4-1.9 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/5151G |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 105 ℃（℉） |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 185 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 95.0 °C | |
| Linear coefficient of thermal expansion | MD：-30到100°C | ISO 11359-2 | 9.5E-05 cm/cm/°C |
| ASTM D-606 | 6.0 cm/cm×10 | ||
| ASTM D696/ISO 11359 | 6.0x10^-5 mm/mm.℃ |