AS(SAN) Luran® 368R 77851 BASF GERMANY
244
- Unit Price:US$ 3,828 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Disassembly rate | 1.569 | ||
| Shrinkage rate | 0.3-0.7 % | ||
| Melting temperature range for pipeline extrusion | 220-240 °C | ||
| Water absorption rate | 0.2 % | ||
| melt mass-flow rate | 12 | ||
| 10 | |||
| Melting temperature range for injection molding | 220-270 °C | ||
| Mold temperature range | 40-80 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 2 KJ/m | ||
| Rockwell hardness | 83 M | ||
| Impact strength of cantilever beam gap | 2 KJ/m | ||
| ball-indentation hardness | 165 Mpa | ||
| Breaking stress | 75 Mpa | ||
| Tensile stress | 125 Mpa | ||
| elongation | 3 % | ||
| Tensile modulus | 3800 Mpa | ||
| Charpy Notched Impact Strength | 18/18 KJ/m | ||
| Tensile creep modulus | 2800 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Relative Arc Track Index CTI Test Solution | CTI 425 | ||
| dielectric constant | 3/2.7 | ||
| Volume resistivity | 10 Ω.cm | ||
| Surface Resistivity | 10 Ω | ||
| Relative Arc Track Index CTI Test Solution | CTI 200M | ||
| dielectric strength | 95 KV/mm | ||
| loss angle | 0.004/0.007 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | 102 °C | ||
| maximum service temperature | 85 °C | ||
| Heat distortion temperature | 98 °C | ||
| Conductivity | 0.17 W/K.m | ||
| Linear coefficient of thermal expansion | 7 | ||
| vicat | 106 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.