AS(SAN) 368R 77851 BASF GERMANY
Luran®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/368R 77851 |
|---|---|---|---|
| elongation | 3 % | ||
| Rockwell hardness | 83 M | ||
| Charpy Notched Impact Strength | 23℃ | 2 KJ/m | |
| Tensile stress | 屈服 | 125 Mpa | |
| Impact strength of cantilever beam gap | 23℃ | 2 KJ/m | |
| ball-indentation hardness | 165 Mpa | ||
| Breaking stress | 75 Mpa | ||
| Tensile modulus | 3800 Mpa | ||
| Charpy Notched Impact Strength | +23/-40℃ | 18/18 KJ/m | |
| Tensile creep modulus | 1000h 伸长率＜＝0.5%+23℃ | 2800 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/368R 77851 |
|---|---|---|---|
| dielectric constant | 100Hz/1MHz | 3/2.7 | |
| Surface Resistivity | 10 Ω | ||
| loss angle | 100Hz/1MHz | 0.004/0.007 | |
| dielectric strength | K20/P20 | 95 KV/mm | |
| Volume resistivity | 10 Ω.cm | ||
| Relative Arc Track Index CTI Test Solution | 试验溶液B | CTI 200M | |
| 试验溶液A/CTIM | CTI 425 |
| physical property | Test Condition | Test Method | BASF GERMANY/368R 77851 |
|---|---|---|---|
| Shrinkage rate | 0.3-0.7 % | ||
| melt mass-flow rate | 200/21 6 | 12 | |
| Mold temperature range | 40-80 °C | ||
| Melting temperature range for pipeline extrusion | 220-240 °C | ||
| melt mass-flow rate | 220/10 | 10 | |
| Disassembly rate | 1.569 | ||
| Water absorption rate | 0.2 % | ||
| Melting temperature range for injection molding | 220-270 °C |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/368R 77851 |
|---|---|---|---|
| vicat | 106 °C | ||
| Heat distortion temperature | 0.45MPa(HDT B) | 102 °C | |
| Linear coefficient of thermal expansion | 纵向(23-80)℃ | 7 | |
| Heat distortion temperature | 1.8MPa(HDT A) | 98 °C | |
| maximum service temperature | 85 °C | ||
| Conductivity | 0.17 W/K.m |