AS(SAN) 80HF LG CHEM KOREA
401
- Unit Price:US$ 2,169 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:heat-resisting|transparent|High mobility
- Application Areas:Electrical appliances|small home appliances|chip|container|Household fan blades|Kitchen utensils|Electrical/Electronic Applications
- Color:--
- Grade:Chemical resistance
Material Certification

Technical Data Sheet
impact performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA2 | 2.80 kJ/m² |
-30°C | ISO 179/1eA2 | 2.00 kJ/m² | |
23°C | ISO 179/1eU2 | 13.0 kJ/m² | |
-30°C | ISO 179/1eU2 | 4.80 kJ/m² | |
Impact strength of cantilever beam gap | -30°C,6.40mm | ASTM D256 | 9.8 J/m |
23°C,6.40mm | ASTM D256 | 9.8 J/m |
flammability | Test Condition | Test Method | Test Result |
---|---|---|---|
UL flame retardant rating | 1.6mm | UL 94 | HB |
3.2mm | UL 94 | HB | |
Burning Behav.atthicknessh | 3.20mm,UL | ISO 12102 | HB |
mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Tensile modulus | 3.20mm | ASTM D638 | 3110 Mpa |
ISO 527-22 | 3300 Mpa | ||
tensile strength | Yield,3.20mm | ASTM D638 | 73.5 Mpa |
Break | ISO 527-22 | 70.0 Mpa | |
Tensile strain | Break,3.20mm | ASTM D638 | 6.0 % |
Break | ISO 527-22 | 6.0 % | |
Bending modulus | 3.20mm | ASTM D790 | 3680 Mpa |
bending strength | 3.20mm | ASTM D790 | 118 Mpa |
thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Hot deformation temperature | 1.8MPa,Unannealed,6.40mm | ASTM D648 | 90.0 °C |
Glass transition temperature | ISO 11357-22 | 110 °C | |
Vicat softening temperature | ASTM D1525 | 100 °C | |
50N | ISO 3062 | 100 °C | |
Linear coefficient of thermal expansion | MD | ISO 11359-22 | 6.7E-05 cm/cm/°C |
TD | ISO 11359-22 | 6.7E-05 cm/cm/°C | |
RTI Elec | UL 746 | 50.0 °C | |
RTI Imp | UL 746 | 50.0 °C | |
RTI Str | UL 746 | 50.0 °C |
Physical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
density | ASTM D792 | 1.07 g/cm³ | |
ISO 11832 | 1070 kg/m3 | ||
melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 3.0 g/10min |
220°C/10.0kg | ASTM D1238 | 29 g/10min | |
230°C/3.8kg | ASTM D1238 | 10 g/10min | |
Melt Volume Flow Rate (MVR) | 220°C/10.0kg | ISO 11332 | 31.0 cm3/10min |
Shrinkage rate | MD:3.20mm | ASTM D955 | 0.40-0.70 % |
Water absorption rate | Saturation | ISO 622 | 0.16 % |
Electrical performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Surface resistivity | IEC 600932 | >1.0E+15 ohms | |
Volume resistivity | IEC 600932 | >1.0E+13 ohms·m | |
Dielectric strength | IEC 60243-12 | 51 KV/mm | |
Compared to the anti leakage trace index | IEC 601122 |
hardness | Test Condition | Test Method | Test Result |
---|---|---|---|
Rockwell hardness | R-Scale | ASTM D785 | 123 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.