Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
AS(SAN) 80HF LG CHEM KOREA
--
Electrical appliances、small home appliances、chip、container、Household fan blades、Kitchen utensils、Electrical/Electronic App
heat-resisting、transparent、High mobility
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodLG CHEM KOREA/80HF
Impact strength of cantilever beam gap23°C,6.40mmASTM D2569.8 J/m
Charpy Notched Impact Strength-30°CISO 179/1eA22.00 kJ/m²
23°CISO 179/1eU213.0 kJ/m²
Impact strength of cantilever beam gap-30°C,6.40mmASTM D2569.8 J/m
Charpy Notched Impact Strength-30°CISO 179/1eU24.80 kJ/m²
23°CISO 179/1eA22.80 kJ/m²
hardnessTest ConditionTest MethodLG CHEM KOREA/80HF
Rockwell hardnessR级ASTM D785123
Mechanical propertiesTest ConditionTest MethodLG CHEM KOREA/80HF
tensile strength Yield,3.20mmASTM D63873.5 Mpa
Tensile strainBreak,3.20mmASTM D6386.0 %
断裂ISO 527-226.0 %
Tensile modulus3.20mmASTM D6383110 Mpa
tensile strength 断裂ISO 527-2270.0 Mpa
Flexural modulus3.20mmASTM D7903680 Mpa
bending strength3.20mmASTM D790118 Mpa
Tensile modulusISO 527-223300 Mpa
Electrical performanceTest ConditionTest MethodLG CHEM KOREA/80HF
Volume resistivityIEC 600932>1.0E+13 ohms·m
dielectric strengthIEC 60243-1251 KV/mm
Compared to the Leakage Tracking Index (CTI)IEC 601122
Surface ResistivityIEC 600932>1.0E+15 ohms
flammabilityTest ConditionTest MethodLG CHEM KOREA/80HF
UL flame retardant rating3.2mmUL 94HB
Burning Behav.atthicknessh3.20mm,ULISO 12102HB
UL flame retardant rating1.6mmUL 94HB
physical property Test ConditionTest MethodLG CHEM KOREA/80HF
melt mass-flow rate200°C/5.0kgASTM D12383.0 g/10min
Shrinkage rateMD：3.20mmASTM D9550.40-0.70 %
Water absorption rate饱和ISO 6220.16 %
Melt volume flow rate220°C/10.0kgISO 1133231.0 cm3/10min
melt mass-flow rate230°C/3.8kgASTM D123810 g/10min
densityASTM D7921.07 g/cm³
melt mass-flow rate220°C/10.0kgASTM D123829 g/10min
densityISO 118321070 kg/m3
Thermal performanceTest ConditionTest MethodLG CHEM KOREA/80HF
vicatASTM D1525100 °C
Heat distortion temperature1.8MPa,未退火,6.40mm，HDTASTM D64890.0 °C
vicat50NISO 3062100 °C
Linear coefficient of thermal expansionTDISO 11359-226.7E-05 cm/cm/°C
MDISO 11359-226.7E-05 cm/cm/°C
Glass Transition TemperatureISO 11357-22110 °C
RTI ImpUL 74650.0 °C
RTI StrUL 74650.0 °C
RTI ElecUL 74650.0 °C