PEI ULTEM™ 2100-1000 SABIC INNOVATIVE US
211
- Unit Price:US$ 21,643 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:11MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜wear resistant｜High rigidity｜Thermal stability｜Flame retardant｜High impact resistance｜Filler: Glass fiber reinforced material｜10% filler by weight｜10% filler by weight
- Application Areas:Fiber grade｜plug｜Laptop case｜Fatigue relief supplies｜Washer
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 114 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI Imp | UL 746 | 170 °C | |
| RTI Str | UL 746 | 170 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTM D648 | 210 °C |
| 1.8MPa,未退火,6.40mm | ASTM D648 | 209 °C | |
| vicat | ASTM D15255 | 223 °C | |
| Linear coefficient of thermal expansion | MD：-20to150°C | ASTME831 | 3.2E-05 cm/cm/°C |
| RTI Elec | UL 746 | 170 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.41mm | UL 94 | V-0 |
| 1.9mm | UL 94 | 5VA | |
| Limiting Oxygen Index | ASTM D2863 | 47 % | |
| NBSSmokeDensity-Flaming,Ds,4min | ASTME662 | 1.80 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 53 J/m |
| 23°C | ASTM D4812 | 480 J/m | |
| 3.20mm | ASTM D256 | 460 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257 | 1E+17 ohms·cm | |
| dielectric strength | 1.60mm,inOil | ASTM D149 | 28 KV/mm |
| dielectric constant | 1kHz | ASTM D150 | 3.50 |
| Dissipation Factor | 1kHz | ASTM D150 | 1.4E-03 |
| 2.45GHz | ASTM D150 | 4.6E-03 | |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 4 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 1 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.34 g/cm³ | |
| melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 7.0 g/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.60 % |
| Water absorption rate | 24hr | ASTM D570 | 0.21 % |
| 平衡,23°C | ASTM D570 | 1.2 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | Break,100mmSpan | ASTM D790 | 200 Mpa |
| Tensile modulus | ASTM D638 | 4690 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 114 Mpa |
| 断裂 | ASTM D638 | 116 Mpa | |
| elongation | 断裂 | ASTM D638 | 6.0 % |
| flexural modulus | 100mmSpan | ASTM D790 | 5170 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.