PBT VALOX™  V4860HR-GY6H015 SABIC INNOVATIVE SHANGHAI

104
  • Unit Price:US$ 8,650 /MT
  • Packaging Specification:
  • Supply Quantity:
    20MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High rigidity｜high strength
  • Application Areas:Home appliance components｜Automotive Applications
  • Color:--
  • Grade:Flame retardant enhanced grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength23°CISO 179/1eA11 kJ/m²
Impact strength of cantilever beam gap-30°CASTM D25674 J/m
Impact strength of cantilever beam gap23°CASTM D25690 J/m
Impact strength of cantilever beam gap-30°CISO 180/1A8.5 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A10 kJ/m²
Dart impact23°C,TotalEnergyASTM D376313.4 J
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.8mmUL 94V-0
mechanical propertiesTest ConditionTest MethodTest Result
bending strengthYield,50.0mmSpanASTM D790174 Mpa
bending strengthBreak,50.0mmSpanASTM D7902.96 Mpa
Fracture bending strainISO 1782.9 %
tensile strengthBreakISO 527-2/5111 Mpa
elongationYieldASTM D6382.3 %
Tensile strainYieldISO 527-2/52.1 %
elongationBreakASTM D6382.3 %
Tensile strainBreakISO 527-2/52.2 %
Bending modulus50.0mmSpanASTM D7906740 Mpa
Bending modulusISO 1787880 Mpa
bending strength--6ISO 178182 Mpa
bending strength--7ISO 178183 Mpa
tensile strengthBreakASTM D638115 Mpa
tensile strengthYieldISO 527-2/5112 Mpa
tensile strengthYieldASTM D638116 Mpa
Tensile modulusISO 527-2/19450 Mpa
Tensile modulusASTM D6389750 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648197 °C
Hot deformation temperature1.8MPa,Unannealed,6.40mmASTM D648205 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af188 °C
Vicat softening temperatureASTM D152512176 °C
Vicat softening temperature--ISO 306/B50176 °C
Vicat softening temperature--ISO 306/B120175 °C
Ball Pressure Test75°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionMD：-40to95°CASTME8312.4E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：23to80°CISO 11359-22.3E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to95°CASTME8311.1E-04 cm/cm/°C
Linear coefficient of thermal expansionTD：23to80°CISO 11359-21.2E-04 cm/cm/°C
Hot deformation temperature0.45MPa,Unannealed,6.40mmASTM D648221 °C
Physical propertiesTest ConditionTest MethodTest Result
densityASTM D7921.64 g/cm³
densityISO 11831.64 g/cm³
Water absorption rateEquilibrium,23°C,50%RHISO 620.060 %
Water absorption rateSaturation,23°CISO 620.19 %
Shrinkage rateTD：3.20mmInternal Method0.50-1.0 %
Shrinkage rateMD：3.20mmInternal Method0.50-0.70 %
Melt Volume Flow Rate (MVR)250°C/5.0kgISO 113312.4 cm3/10min
melt mass-flow rate250°C/5.0kgASTM D123818 g/10min
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.