Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT V4860HR-GY6H015 SABIC INNOVATIVE SHANGHAI
VALOX™
Home appliance components、Automotive Applications
High rigidity、high strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/V4860HR-GY6H015 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 11 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 74 J/m |
| 23°C | ASTM D256 | 90 J/m | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 13.4 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.5 kJ/m² |
| 23°C | ISO 180/1A | 10 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/V4860HR-GY6H015 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 9450 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 111 Mpa |
| elongation | 屈服 | ASTM D638 | 2.3 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 2.1 % |
| tensile strength | 断裂 | ASTM D638 | 115 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 6740 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 112 Mpa |
| Tensile modulus | ASTM D638 | 9750 Mpa | |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 174 Mpa |
| elongation | 断裂 | ASTM D638 | 2.3 % |
| bending strength | --6 | ISO 178 | 182 Mpa |
| --7 | ISO 178 | 183 Mpa | |
| Flexural modulus | ISO 178 | 7880 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.2 % |
| Fracture bending strain | ISO 178 | 2.9 % | |
| tensile strength | 屈服 | ASTM D638 | 116 Mpa |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 2.96 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/V4860HR-GY6H015 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/V4860HR-GY6H015 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 12.4 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.060 % |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.50-1.0 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.19 % |
| density | ASTM D792 | 1.64 g/cm³ | |
| ISO 1183 | 1.64 g/cm³ | ||
| melt mass-flow rate | 250°C/5.0kg | ASTM D1238 | 18 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/V4860HR-GY6H015 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 205 °C |
| vicat | ASTM D152512 | 176 °C | |
| -- | ISO 306/B120 | 175 °C | |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | TD：-40to95°C | ASTME831 | 1.1E-04 cm/cm/°C |
| MD：-40到95°C | ASTME831 | 2.4E-05 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 176 °C |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 188 °C |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 2.3E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 221 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 197 °C | |
| Linear coefficient of thermal expansion | TD：23to80°C | ISO 11359-2 | 1.2E-04 cm/cm/°C |
Contact Us
Get App