Plastic Raw Materials
TPEE

TPEE RITEFLEX® 655 CELANESE USA

197
  • Unit Price:US$ 3,952 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    48.9MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:UV resistance
  • Application Areas:Automotive components｜High temperature hot plugging adhesive
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5mmUL 94HB
elastomerTest ConditionTest MethodTest Result
tear strengthASTM D624212 kN/m
tear strengthFlowISO 34-1120 kN/m
Permanent compression deformation23°CASTM D395<1.0 %
Shore hardness--Internal Method48 %
Shore hardness--ASTM D263248 %
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusISO 527-2/1A/1175 Mpa
tensile strengthYieldISO 527-2/1A/5015.0 Mpa
tensile strengthBreak,23°CASTM D63825.2 Mpa
tensile strengthBreakISO 527-2/1A/5030.0 Mpa
tensile strength5.0%StrainISO 527-28.00 Mpa
tensile strength10%StrainISO 527-212.0 Mpa
tensile strength50%StrainISO 527-2/1A/5015.0 Mpa
Tensile strainYieldISO 527-2/1A/5028 %
elongationBreak,23°CASTM D638430 %
Tensile strainBreakISO 527-2/1A/50>300 %
Tensile modulus23°CASTM D638241 Mpa
Bending modulus-40°CISO 178700 Mpa
Bending modulus23°CISO 178175 Mpa
Bending modulus100°CISO 17886.0 Mpa
bending strength3.5%StrainISO 1787.00 Mpa
bending strength23°CISO 17810.0 Mpa
RossFlexInternal Method>1.0E+6 cycles
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B75.0 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A48.0 °C
Glass transition temperatureASTM D3418-56.7 °C
Vicat softening temperatureASTM D1525181 °C
Melting temperatureASTM D3418200 °C
Melting temperatureISO 11357-3200 °C
Linear coefficient of thermal expansionMDISO 11359-22E-04 cm/cm/°C
Linear coefficient of thermal expansionTDISO 11359-21.7E-04 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Specific volumeASTM D7920.842 cm³/g
melt mass-flow rateASTM D12387.0to11 g/10min
melt mass-flow rate220°C/2.16kgISO 113310 g/10min
Shrinkage rateMDASTM D9551.5 %
Shrinkage rateTDISO 294-41.7-2.1 %
Shrinkage rateMDISO 294-41.6-1.9 %
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityIEC 600934E+15 ohms
Volume resistivityASTM D2575E+12 ohms·cm
Volume resistivityIEC 600934E+12 ohms·cm
Dielectric strengthASTM D14914 KV/mm
Dielectric strengthIEC 60243-114 KV/mm
Relative permittivity1MHzIEC 602504.40
Dissipation factor1MHzIEC 602500.040
Compared to the anti leakage trace indexASTM D3638PLC 0
Compared to the anti leakage trace indexIEC 60112PLC 0
hardnessTest ConditionTest MethodTest Result
Shore hardnessShoreDASTM D224055
Shore hardnessShoreD,15SecISO 86855
Supplementary InformationTest ConditionTest MethodTest Result
tear strengthKg/m217.2 kN/m
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.