TPEE 655 CELANESE USA

RITEFLEX®

Automotive components,High temperature hot plugging adhesive

UV resistance

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

Supplementary Information	Test Condition	Test Method	CELANESE USA/655
tear strength		Kg/m	217.2 kN/m

hardness	Test Condition	Test Method	CELANESE USA/655
Shore hardness	ShoreD	ASTM D2240	55
Shore hardness		ShoreD,15Sec	ISO 868	55

thermal performance	Test Condition	Test Method	CELANESE USA/655
Glass transition temperature		ASTM D3418	-56.7 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	75.0 °C
Hot deformation temperature		1.8MPa,Unannealed	ISO 75-2/A	48.0 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.7E-04 cm/cm/°C
Linear coefficient of thermal expansion		MD	ISO 11359-2	2E-04 cm/cm/°C
Melting temperature		ASTM D3418	200 °C
Melting temperature			ISO 11357-3	200 °C
Vicat softening temperature		ASTM D1525	181 °C

mechanical properties	Test Condition	Test Method	CELANESE USA/655
Bending modulus	100°C	ISO 178	86.0 Mpa
		-40°C	ISO 178	700 Mpa
		23°C	ISO 178	175 Mpa
bending strength	3.5%Strain	ISO 178	7.00 Mpa
bending strength		23°C	ISO 178	10.0 Mpa
elongation	Break,23°C	ASTM D638	430 %
RossFlex		Internal Method	>1.0E+6 cycles
Tensile modulus		ISO 527-2/1A/1	175 Mpa
Tensile modulus		23°C	ASTM D638	241 Mpa
Tensile strain	Yield	ISO 527-2/1A/50	28 %
Tensile strain		Break	ISO 527-2/1A/50	>300 %
tensile strength	Break	ISO 527-2/1A/50	30.0 Mpa
		5.0%Strain	ISO 527-2	8.00 Mpa
		10%Strain	ISO 527-2	12.0 Mpa
		50%Strain	ISO 527-2/1A/50	15.0 Mpa
		Break,23°C	ASTM D638	25.2 Mpa
		Yield	ISO 527-2/1A/50	15.0 Mpa

Electrical performance	Test Condition	Test Method	CELANESE USA/655
Compared to the anti leakage trace index		IEC 60112	PLC 0
Compared to the anti leakage trace index			ASTM D3638	PLC 0
Dielectric strength		IEC 60243-1	14 KV/mm
Dielectric strength			ASTM D149	14 KV/mm
Dissipation factor	1MHz	IEC 60250	0.040
Relative permittivity	1MHz	IEC 60250	4.40
Surface resistivity		IEC 60093	4E+15 ohms
Volume resistivity		ASTM D257	5E+12 ohms·cm
Volume resistivity			IEC 60093	4E+12 ohms·cm

Physical properties	Test Condition	Test Method	CELANESE USA/655
melt mass-flow rate		ASTM D1238	7.0to11 g/10min
melt mass-flow rate		220°C/2.16kg	ISO 1133	10 g/10min
Shrinkage rate	MD	ISO 294-4	1.6-1.9 %
		MD	ASTM D955	1.5 %
		TD	ISO 294-4	1.7-2.1 %
Specific volume		ASTM D792	0.842 cm³/g

impact performance	Test Condition	Test Method	CELANESE USA/655
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	NoBreak

flammability	Test Condition	Test Method	CELANESE USA/655
UL flame retardant rating	1.5mm	UL 94	HB

elastomer	Test Condition	Test Method	CELANESE USA/655
Permanent compression deformation	23°C	ASTM D395	<1.0 %
Shore hardness	--	ASTM D2632	48 %
Shore hardness		--	Internal Method	48 %
tear strength	Flow	ISO 34-1	120 kN/m
tear strength			ASTM D624	212 kN/m