PA66

PA66 LATAMID 66 H2 G/60 LATI ITALY

206

Unit Price:US$ 4,206 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
21.2MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Filler: Glass fiber reinforced material｜60% filler by weight
Application Areas:--
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	255 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	235 °C
Continuous use temperature			135 °C
Vicat softening temperature		ISO 306/B50	240 °C
Linear coefficient of thermal expansion	MD：30to100°C	ISO 11359-2	6E-06 cm/cm/°C

other	Test Condition	Test Method	Test Result
characteristic			高刚性
purpose			家用电器配件

Supplementary Information	Test Condition	Test Method	Test Result
dimensional stability			63.0

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD:2.00mm	ISO 294-4	0.60-0.85 %
Shrinkage rate	Shrinkage rate	MD:2.00mm	ISO 294-4	0.30-0.50 %
Water absorption rate	23°C,24hr	ISO 62	0.26 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Break,60°C	ISO 527-2/5	2.6 %
	Tensile strain	Break,90°C	ISO 527-2/5	5.7 %
		Tensile strain	Break,120°C	ISO 527-2/5	7.0 %
		Tensile strain	Tensile strain	Break,150°C	ISO 527-2/5	7.5 %
Tensile modulus	120°C	ISO 527-2/1	6600 Mpa
Tensile modulus	Tensile modulus	150°C	ISO 527-2/1	5800 Mpa
tensile strength	Break	ISO 527-2/5	-- Mpa
	tensile strength	Break,23°C	ISO 527-2/5	235 Mpa
		tensile strength	Break,60°C	ISO 527-2/5	180 Mpa
			tensile strength	Break,90°C	ISO 527-2/5	130 Mpa
				tensile strength	Break,120°C	ISO 527-2/5	100 Mpa
				tensile strength	tensile strength	Break,150°C	ISO 527-2/5	75.0 Mpa
Tensile strain	Break	ISO 527-2/5	-- %
Tensile strain	Tensile strain	Break,23°C	ISO 527-2/5	2.2 %
Tensile modulus	--	ISO 527-2/1	-- Mpa
	Tensile modulus	23°C	ISO 527-2/1	22500 Mpa
		Tensile modulus	60°C	ISO 527-2/1	18000 Mpa
		Tensile modulus	Tensile modulus	90°C	ISO 527-2/1	11000 Mpa

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	55 kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.