PA66 66 H2 G/60 LATI ITALY
LATAMID
--
Filler: Glass fiber reinf、60% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LATI ITALY/66 H2 G/60 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 55 kJ/m² |
| Supplementary Information | Test Condition | Test Method | LATI ITALY/66 H2 G/60 |
|---|---|---|---|
| dimensional stability | 63.0 |
| Mechanical properties | Test Condition | Test Method | LATI ITALY/66 H2 G/60 |
|---|---|---|---|
| Tensile modulus | 60°C | ISO 527-2/1 | 18000 Mpa |
| tensile strength | 断裂 | ISO 527-2/5 | -- Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 2.2 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 235 Mpa |
| Tensile modulus | 90°C | ISO 527-2/1 | 11000 Mpa |
| 23°C | ISO 527-2/1 | 22500 Mpa | |
| Tensile strain | 断裂,120°C | ISO 527-2/5 | 7.0 % |
| Tensile modulus | 150°C | ISO 527-2/1 | 5800 Mpa |
| Tensile strain | 断裂,150°C | ISO 527-2/5 | 7.5 % |
| Tensile modulus | 120°C | ISO 527-2/1 | 6600 Mpa |
| tensile strength | 断裂,90°C | ISO 527-2/5 | 130 Mpa |
| 断裂,120°C | ISO 527-2/5 | 100 Mpa | |
| 断裂,150°C | ISO 527-2/5 | 75.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | -- % |
| 断裂,60°C | ISO 527-2/5 | 2.6 % | |
| 断裂,90°C | ISO 527-2/5 | 5.7 % | |
| Tensile modulus | -- | ISO 527-2/1 | -- Mpa |
| tensile strength | 断裂,60°C | ISO 527-2/5 | 180 Mpa |
| other | Test Condition | Test Method | LATI ITALY/66 H2 G/60 |
|---|---|---|---|
| characteristic | 高刚性 | ||
| purpose | 家用电器配件 |
| physical property | Test Condition | Test Method | LATI ITALY/66 H2 G/60 |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.30-0.50 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.26 % |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.60-0.85 % |
| Thermal performance | Test Condition | Test Method | LATI ITALY/66 H2 G/60 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 255 °C |
| vicat | ISO 306/B50 | 240 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 235 °C |
| Continuous use temperature | 135 °C | ||
| Linear coefficient of thermal expansion | MD：30到100°C | ISO 11359-2 | 6E-06 cm/cm/°C |