SPS

SPS XAREC™ SP140 IDEMITSU JAPAN

307

Unit Price:US$ 3,575 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜Glass fiber reinforced
Application Areas:Household daily necessities｜Electrical applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180	29 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180	10 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	33 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	10 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	120 Mpa
Bending modulus		ISO 178	6100 Mpa
Tensile strain	Break	ISO 527-2	2.5 %
tensile strength	Break	ISO 527-2	75.0 Mpa
Tensile modulus		ISO 527-2	6500 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			120 °C
drying time			3.0 to 5.0 hr
Processing (melt) temperature			280 to 310 °C
Mold temperature			130 to 155 °C

thermal performance	Test Condition	Test Method	Test Result
RTI		UL 746	50.0 °C
RTI Imp		UL 746	50.0 °C
RTI Elec		UL 746	50.0 °C
Linear coefficient of thermal expansion	Across Flow : -30 to 30°C	TMA	7.1E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : -30 to 30°C	TMA	3.3E-5 cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	175 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	255 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.010 %
Shrinkage rate	Flow	Internal Method	0.20 - 0.50 %
Shrinkage rate	Shrinkage rate	横向Flow	Internal Method	0.30 - 0.70 %
density		ISO 1183	1.31 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Arc resistance		ASTM D495	PLC 6
Compared to the anti leakage trace index		IEC 60112	PLC 0
Dissipation factor	1 MHz	IEC 60250	< 1.0E-3
Dielectric constant	1 MHz	IEC 60250	3.10
Dielectric strength		ASTM D149	50 KV/mm
Volume resistivity		IEC 60093	> 1.0E+16 ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

SPS XAREC™ SP140 IDEMITSU JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet