Material Description
- Material Properties:High gloss｜High mobility｜Fatigue resistance｜Moderate impact resistance
- Application Areas:battery｜Electrical enclosure｜Electrical appliances｜TV casing｜furniture｜Toy｜Footwear｜battery｜Electrical enclosure｜Electrical appliances｜TV casing｜furniture｜Toy｜Footwear
- Color:--
- Grade:Injection grade
Material Certification
TDS
TDS_ISO
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R-Sale,23°C | ASTM D785 | 110 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, Annealed, 12.7 mm | ASTM D648 | 86 °C |
| Vicat softening temperature | ASTM D1525 | 103 °C | |
| High arc combustion index | 1.57 mm | UL 746 | |
| High voltage arc tracing rate | 1.57 mm | UL 746 | mm/min |
| Hot wire ignition | 1.57 mm | UL 746 | sec |
| UL flame retardant rating | 1.59 mm | UL 94 | HB |
| Hot deformation temperature | 1.8MPa,Annealed,12.7mm | ASTM D648 | 86.0 °C |
| Vicat softening temperature | ASTM D15255 | 103 °C | |
| RTI Elec | 1.6mm | UL 746 | 60.0 °C |
| RTI Imp | 1.6mm | UL 746 | 60.0 °C |
| RTI Str | 1.6mm | UL 746 | 60.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.03 g/cm³ | |
| melt mass-flow rate | 200℃/5.0 kg | ASTM D1238 | 1.8 g/10 min |
| 220℃/10.0 kg | ASTM D1238 | 18 g/10 min | |
| Shrinkage rate | MD | ASTM D955 | < 0.40 % |
| Water absorption rate | Saturation | ASTM D570 | < 0.30 % |
| density | ASTM D792 | 1.03 g/cm³ | |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 1.8 g/10min |
| 220°C/10.0kg | ASTM D1238 | 18 g/10min | |
| Shrinkage rate | MD | ASTM D955 | <0.40 % |
| Water absorption rate | Saturation | ASTM D570 | <0.30 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| High arc combustion index | 1.57mm | UL 746 | |
| High voltage arc tracing rate | 1.57mm | UL 746 | mm/min |
| Hot wire ignition | 1.57mm | UL 746 | sec |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | Yield, 23℃ | ASTM D790 | 68.9 Mpa |
| Impact strength of cantilever beam gap | 23℃, 3.18 mm | ASTM D256 | 260 J/m |
| 23℃, 6.35 mm | ASTM D256 | 230 J/m | |
| Rockwell hardness | R-Scale, 23℃ | ASTM D785 | 110 |
| tensile strength | Yield, 23℃, 3.18 mm | ASTM D638 | 40 Mpa |
| Break, 23℃, 3.18 mm | ASTM D638 | 35.2 Mpa | |
| elongation | Break, 23℃, 3.18 mm | ASTM D638 | 30 % |
| Bending modulus | 23℃ | ASTM D790 | 2340 Mpa |
| 23°C | ASTM D790 | 2340 Mpa | |
| bending strength | Yield,23°C | ASTM D790 | 68.9 Mpa |
| tensile strength | Yield,23°C,3.18mm | ASTM D638 | 40.0 Mpa |
| Break,23°C,3.18mm | ASTM D638 | 35.2 Mpa | |
| elongation | Break,23°C,3.18mm | ASTM D638 | 30 % |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 260 J/m |
| 23°C,6.35mm | ASTM D256 | 230 J/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.