Material Properties:high viscosity｜wear resistant｜transparent｜High mobility｜Weather resistance｜currency
Application Areas:Electrical field｜Electronic field｜Household appliances｜Household appliances
Color:--
Grade:Injection grade

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.41	g/cm³
melt mass-flow rate	190℃/2.16kg	ISO 1133	8	cm³/10min
Shrinkage rate	flow	ASTM D955	2.2	%
	Shrinkage rate	flow	ISO 294-4	1.9	%
		Shrinkage rate	Across flow	ASTM D955	1.8	%
		Shrinkage rate	Shrinkage rate	Across flow	ISO 294-4	1.7	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1A/1	2750	MPa
tensile strength	Yield	ISO 527-2/1A/50	63	MPa
tensile strength	tensile strength	Break,23℃	ASTM D638	60.7	MPa
Tensile strain	Yield	ISO 527-2/1A/50	10	%
Bending modulus	23℃	ISO 178	2490	MPa
Impact strength of simply supported beam without notch	-30℃	ISO 179/1eA	4	kJ/m²
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	110	℃
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	91	℃
Vicat softening temperature		ISO 306/B50	161	℃
Linear coefficient of thermal expansion	flow	ISO 11359-2	0.00011	cm/cm/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Transverse	ISO 11359-2	0.00012	cm/cm/℃

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.