ABS CYCOLAC™ FR15U SABIC INNOVATIVE US

352

Unit Price:US$ 7,492 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
55MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜UV resistance
Application Areas:Automotive sector｜Electronic field｜Electrical field
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ASTM D256	210 J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	28.5 J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	12 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	2.8mm	UL 94	5VA
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	50.0mmSpan	ASTM D790	2340 Mpa
Bending modulus	Bending modulus		ISO 178	2260 Mpa
bending strength		ISO 178	63.3 Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	67.6 Mpa
Tensile strain	Break	ISO 527-2/50	22 %
elongation	Break	ASTM D638	17 %
elongation	elongation	Yield	ASTM D638	2.4 %
tensile strength	Break	ASTM D638	30.3 Mpa
Tensile modulus		ASTM D638	2070 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2210 Mpa
tensile strength	Yield	ASTM D638	37.9 Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	41.1 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	9.2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	9E-05 cm/cm/°C
Vicat softening temperature		ISO 306/B50	92.0 °C
RTI Str		UL 746	90.0 °C
RTI Imp		UL 746	85.0 °C
RTI Elec		UL 746	90.0 °C
Vicat softening temperature		ASTM D15258	93.9 °C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	75.0 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	86.1 °C

Physical properties	Test Condition	Test Method	Test Result
MeltViscosity	200°C,1000sec^-1	ASTM D3835	320 Pa·s
density		ASTM D792	1.19 g/cm³
density	density		ISO 1183	1.19 g/cm³
melt mass-flow rate	230°C/3.8kg	ASTM D1238	3.3 g/10min
melt mass-flow rate	melt mass-flow rate	220°C/5.0kg	ISO 1133	7.0 g/10min
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	40.0 cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %

Electrical performance	Test Condition	Test Method	Test Result
Hot wire ignition	HWI	UL 746	PLC 2
High voltage arc tracing rate	HVTR	UL 746	PLC 4
High arc combustion index	HAI	UL 746	PLC 4
Compared to the anti leakage trace index	CTI	UL 746	PLC 1
Arc resistance		ASTM D495	PLC7
Dielectric strength	3.20mm,in Oil	IEC 60243-1	20 KV/mm
Volume resistivity		IEC 60093	>1.0E+14 ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.