Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS FR15U SABIC INNOVATIVE US
CYCOLAC™
Automotive sector、Electronic field、Electrical field
Flame retardant、UV resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/FR15U |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 28.5 J |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 210 J/m |
| 23°C | ISO 180/1A | 12 kJ/m² |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/FR15U |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 |
| Volume resistivity | IEC 60093 | >1.0E+14 ohms·cm | |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 20 KV/mm |
| arc resistance | ASTM D495 | PLC7 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 1 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/FR15U |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2210 Mpa | |
| ASTM D638 | 2070 Mpa | ||
| tensile strength | 屈服 | ISO 527-2/50 | 41.1 Mpa |
| elongation | 断裂 | ASTM D638 | 17 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 67.6 Mpa |
| elongation | 屈服 | ASTM D638 | 2.4 % |
| bending strength | ISO 178 | 63.3 Mpa | |
| Flexural modulus | ISO 178 | 2260 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 30.3 Mpa |
| 屈服 | ASTM D638 | 37.9 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 22 % |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2340 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/FR15U |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| 2.8mm | UL 94 | 5VA |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/FR15U |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 3.3 g/10min |
| 220°C/5.0kg | ISO 1133 | 7.0 g/10min | |
| density | ASTM D792 | 1.19 g/cm³ | |
| ISO 1183 | 1.19 g/cm³ | ||
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 40.0 cm3/10min |
| MeltViscosity | 200°C,1000sec^-1 | ASTM D3835 | 320 Pa·s |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/FR15U |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 9.2E-05 cm/cm/°C |
| vicat | ASTM D15258 | 93.9 °C | |
| ISO 306/B50 | 92.0 °C | ||
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 86.1 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 9E-05 cm/cm/°C |
| RTI Imp | UL 746 | 85.0 °C | |
| RTI Str | UL 746 | 90.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 75.0 °C |
| RTI Elec | UL 746 | 90.0 °C |