PPA AMODEL® AFA-6133 BK324 SOLVAY USA
216
- Unit Price:US$ 5,624 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Filler: Glass fiber reinforced material｜33% filler by weight
- Application Areas:Vehicle electronics｜Application in the automotive field｜Laptop case｜Spool
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.30 % | |
| ASTM D955 | 0.60 % | ||
| Water absorption rate | ASTM D570 | 0.20 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 16100 Mpa | |
| ISO 527-2 | 14500 Mpa | ||
| ISO 527-2 | 9170 Mpa | ||
| ISO 527-2 | 5930 Mpa | ||
| ISO 527-2 | 5100 Mpa | ||
| tensile strength | ASTM D638 | 199 Mpa | |
| ISO 527-2 | 186 Mpa | ||
| ISO 527-2 | 114 Mpa | ||
| ISO 527-2 | 75.2 Mpa | ||
| ISO 527-2 | 63.4 Mpa | ||
| elongation | ASTM D638 | 1.7 % | |
| Tensile strain | ISO 527-2 | 1.6 % | |
| ISO 527-2 | 2.4 % | ||
| ISO 527-2 | 5.1 % | ||
| ISO 527-2 | 4.9 % | ||
| Flexural modulus | ASTM D790 | 13100 Mpa | |
| ISO 178 | 12600 Mpa | ||
| ISO 178 | 8070 Mpa | ||
| ISO 178 | 4960 Mpa | ||
| ISO 178 | 4620 Mpa | ||
| bending strength | ASTM D790 | 224 Mpa | |
| ISO 178 | 259 Mpa | ||
| ISO 178 | 161 Mpa | ||
| ISO 178 | 101 Mpa | ||
| ISO 178 | 87.6 Mpa | ||
| compressive strength | ASTM D695 | 145 Mpa | |
| shear strength | ASTM D732 | 80.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ISO 180/1U | 44 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 46 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| UL 746 | PLC 0 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 0 | |
| UL 746 | PLC 0 | ||
| UL 746 | PLC 0 | ||
| Surface Resistivity | ASTM D257 | 1E+15 ohms | |
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 24 KV/mm | |
| dielectric constant | ASTM D150 | 4.40 | |
| ASTM D150 | 4.10 | ||
| Dissipation Factor | ASTM D150 | 0.011 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 1 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/Af | 282 °C | |
| ASTM D648 | 277 °C | ||
| melting temperature | ASTM D3418 | 310 °C | |
| ISO 11357-3 | 310 °C | ||
| Linear coefficient of thermal expansion | ASTME831 | 1.7E-05 cm/cm/°C | |
| ASTME831 | 7E-06 cm/cm/°C | ||
| ASTME831 | 6.4E-05 cm/cm/°C | ||
| ASTME831 | 1.1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.