Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPA AFA-6133 BK324 SOLVAY USA
AMODEL®
Vehicle electronics、Application in the automo、Laptop case、Spool
Filler: Glass fiber reinf、33% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY USA/AFA-6133 BK324 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 44 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 46 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/AFA-6133 BK324 |
|---|---|---|---|
| Tensile modulus | 175°C | ISO 527-2 | 5100 Mpa |
| 23°C | ISO 527-2 | 14500 Mpa | |
| tensile strength | Yield,175°C | ISO 527-2 | 63.4 Mpa |
| bending strength | 175°C | ISO 178 | 87.6 Mpa |
| Flexural modulus | ASTM D790 | 13100 Mpa | |
| Tensile modulus | 150°C | ISO 527-2 | 5930 Mpa |
| bending strength | 150°C | ISO 178 | 101 Mpa |
| tensile strength | 屈服,150°C | ISO 527-2 | 75.2 Mpa |
| bending strength | 100°C | ISO 178 | 161 Mpa |
| elongation | 断裂 | ASTM D638 | 1.7 % |
| Flexural modulus | 23°C | ISO 178 | 12600 Mpa |
| tensile strength | Yield,100°C | ISO 527-2 | 114 Mpa |
| Tensile strain | 断裂,150°C | ISO 527-2 | 5.1 % |
| bending strength | ASTM D790 | 224 Mpa | |
| Flexural modulus | 100°C | ISO 178 | 8070 Mpa |
| Tensile strain | 断裂,175°C | ISO 527-2 | 4.9 % |
| Tensile modulus | 100°C | ISO 527-2 | 9170 Mpa |
| tensile strength | ASTM D638 | 199 Mpa | |
| Tensile strain | 断裂,24°C | ISO 527-2 | 2.4 % |
| Tensile modulus | ASTM D638 | 16100 Mpa | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 1.6 % |
| Flexural modulus | 150°C | ISO 178 | 4960 Mpa |
| bending strength | 23°C | ISO 178 | 259 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 186 Mpa |
| Flexural modulus | 175°C | ISO 178 | 4620 Mpa |
| shear strength | ASTM D732 | 80.0 Mpa | |
| compressive strength | ASTM D695 | 145 Mpa |
| Electrical performance | Test Condition | Test Method | SOLVAY USA/AFA-6133 BK324 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| Surface Resistivity | ASTM D257 | 1E+15 ohms | |
| Dissipation Factor | 1MHz | ASTM D150 | 0.011 |
| Hot wire ignition (HWI) | 1.5mm | UL 746 | PLC 0 |
| High arc combustion index (HAI) | 1.5mm | UL 746 | PLC 0 |
| dielectric constant | 1MHz | ASTM D150 | 4.10 |
| Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 0 |
| dielectric constant | 100Hz | ASTM D150 | 4.40 |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 0 |
| 0.75mm | UL 746 | PLC 0 | |
| Hot wire ignition (HWI) | 0.75mm | UL 746 | PLC 0 |
| dielectric strength | 3.17mm | ASTM D149 | 24 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 1 |
| flammability | Test Condition | Test Method | SOLVAY USA/AFA-6133 BK324 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SOLVAY USA/AFA-6133 BK324 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.30 % |
| Water absorption rate | 24hr | ASTM D570 | 0.20 % |
| Shrinkage rate | TD | ASTM D955 | 0.60 % |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/AFA-6133 BK324 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 282 °C |
| melting temperature | ISO 11357-3 | 310 °C | |
| Linear coefficient of thermal expansion | TD：100到200°C | ASTME831 | 1.1E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ASTM D648 | 277 °C |
| Linear coefficient of thermal expansion | MD：100到200°C | ASTME831 | 7E-06 cm/cm/°C |
| TD：0to100°C | ASTME831 | 6.4E-05 cm/cm/°C | |
| melting temperature | ASTM D3418 | 310 °C | |
| Linear coefficient of thermal expansion | MD：0to100°C | ASTME831 | 1.7E-05 cm/cm/°C |
Contact Us
Get App