PA66 Zytel® 408HS DUPONT USA
195
- Unit Price:US$ 5,631 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:30MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:enhance｜Toughening｜Thermal stability｜High impact resistance｜High temperature resistance
- Application Areas:Industrial machinery｜Automotive sector
- Color:--
- Grade:Special level
Material Certification
Technical Data Sheet
Compare
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 注塑级.良好的热稳定性 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | 255 ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 7×10-5 mm/mm.℃ | |
| Heat Deflection Temperature | (0.5)×106Pa | ASTM D-648 | DAM｜230 °C |
| (0.5)×106Pa | ASTM D-648 | 50%RH｜- °C | |
| UL flame retardant rating | UL 94 | DAM｜94 | |
| UL 94 | 50%RH｜HB | ||
| melting temperature | ASTM D-2177 | DAM｜270 °C | |
| ASTM D-2177 | 50%RH｜- °C | ||
| Linear coefficient of thermal expansion | ASTM D-696 | DAM｜7×10-5 m/m/℃ | |
| ASTM D-696 | 50%RH｜- m/m/℃ | ||
| Load deformation | 13.8MPa，50℃ | ASTM D-621 | DAM｜1.4 % |
| 13.8MPa，50℃ | ASTM D-621 | 50%RH｜- % | |
| melting temperature | Fisher Johns法 | ASTM D-789 | 255 °C |
| Fisher Johns法 | ASTM D-789 | 255 °C | |
| Heat Deflection Temperature | 18×106Pa | ASTM D-648 | DAM｜75 °C |
| 18×106Pa | ASTM D-648 | 50%RH｜- °C | |
| brittle temperature | ASTM D-746 | DAM｜-104 °C | |
| ASTM D-746 | 50%RH｜-84 °C | ||
| Heat Deflection Temperature | 66 psi， 未退火 | ASTM D648 | 184 °C |
| Linear coefficient of thermal expansion | 平行流动方向 | ASTM E831 | 0.00010 cm/cm/ ℃ |
| UL flame retardant rating | UL 94 | HB | |
| Limiting Oxygen Index | ASTM D2863 | 23 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 24小时浸渍(23℃) | ASTM D-570 | DAM｜1.2 % |
| 24小时浸渍(23℃) | ASTM D-570 | 50%RH｜- % | |
| 饱和(23℃) | ASTM D-570 | DAM｜7.0 % | |
| 饱和(23℃) | ASTM D-570 | 50%RH｜- % |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index (LOI) | ASTM D-2863 | DAM｜19 % | |
| ASTM D-2863 | 50%RH｜20 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | ASTM D150/IEC 60250 | 3.1 | |
| volume resistivity | ASTM D257/IEC 60093 | 10 Ω.cm | |
| ASTM D-257 | DAM｜1013 Ω.m | ||
| ASTM D-257 | 50%RH｜1013 Ω.m | ||
| dielectric constant | 103Hz(cps) | ASTM D-150 | DAM｜3.1 |
| 100Hz(cps) | ASTM D-150 | 50%RH｜4.8 | |
| Dissipation Factor | 100Hz(cps) | ASTM D-150 | DAM｜0.02 |
| 100Hz(cps) | ASTM D-150 | 50%RH｜0.1 | |
| 103Hz(cps) | ASTM D-150 | DAM｜0.02 | |
| 103Hz(cps) | ASTM D-150 | 50%RH｜0.11 | |
| 106Hz(cps) | ASTM D-150 | DAM｜0.02 | |
| 106Hz(cps) | ASTM D-150 | 50%RH｜0.10 | |
| dielectric constant | 106Hz(cps) | ASTM D-150 | DAM｜2.9 |
| 106Hz(cps) | ASTM D-150 | 50%RH｜3.3 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.09 | |
| Water absorption rate | ASTM D570/ISO 62 | 1.2 % | |
| 24小时 | ASTM D570 | 1.2 % | |
| 饱和 | ASTM D570 | 7.0 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Elongation at break | ASTM D638/ISO 527 | 80 % | |
| tensile strength | ASTM D638/ISO 527 | 62.1 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 60.7 % | |
| Hardness (Rockwell R) | ASTM D-785 | 50%RH｜R102 | |
| elongation at yield | ASTM D-638 | DAM｜5 % | |
| ASTM D-638 | 50%RH｜15 % | ||
| tensile strength | 23℃，屈服 | DAM｜60.7 Mpa | |
| 23℃，屈服 | 50%RH｜51.7 Mpa | ||
| Impact strength of cantilever beam gap | 长试样23℃ | ASTM D-1822 | DAM｜550 kJ/m² |
| 长试样23℃ | ASTM D-1822 | 50%RH｜1680 kJ/m² | |
| 短试样23℃ | ASTM D-1822 | DAM｜189 kJ/m² | |
| 短试样23℃ | ASTM D-1822 | 50%RH｜265 kJ/m² | |
| tensile strength | 23℃ | ASTM D-638 | DAM｜62.1 Mpa |
| Elongation at break | 23℃ | ASTM D-638 | DAM｜80 % |
| 23℃ | ASTM D-638 | 50%RH｜270 % | |
| Rubbing modulus | 23℃ | ASTM D-790 | DAM｜1965 Mpa |
| 23℃ | ASTM D-790 | 50%RH｜1103 Mpa | |
| Hardness (Rockwell M) | ASTM D-785 | DAM｜M71 | |
| ASTM D-785 | 50%RH｜M50 | ||
| Impact strength of cantilever beam gap | 23℃ | ASTM D-256 | DAM｜230 J/m |
| 23℃ | ASTM D-256 | 50%RH｜240 J/m | |
| Shore hardness | ASTM D-676 | DAM｜83 | |
| ASTM D-676 | 50%RH｜76 | ||
| Hardness (Rockwell R) | ASTM D-785 | DAM｜R115 | |
| tensile strength | 23℃ | ASTM D-638 | 50%RH｜51.7 Mpa |
| 屈服 | ASTM D638 | 62.7 Mpa | |
| flexural modulus | ASTM D790 | 2070 Mpa | |
| Elongation at break | ASTM D638 | 50 % | |
| Impact strength of cantilever beam gap | ASTM D256 | 134 J/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.