other	Test Condition	Test Method	Test Result	Test Unit
characteristic			耐热性、挤出
Other performance	Test Condition	Test Method	Test Result	Test Unit
Bez		ASTM D-1003	0.3	%
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate		ASTM D-570	0.3	%
melt mass-flow rate	230℃/3.8kgs	ASTM D-1238	2.1	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness		ASTM D785	105
Bending modulus		ASTM D790/ISO 178	35000	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D-638	7	%
tensile strength	tensile strength		ASTM D-638	770	kg/cm
Impact strength of cantilever beam gap		ASTM D-256	1.6	kg.cm/cm
Rockwell hardness		ASTM D-785	105	M Scale
bending strength		ASTM D-790	1240	kg/cm
Bending modulus		ASTM D-790	35000	kg/cm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility (rate)		UL 94	HB
Hot deformation temperature	HDT	ASTM D648/ISO 75	106	℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	97	℃（℉）
Vicat softening temperature		ASTM D1525/ISO R306	118	℃（℉）
Hot deformation temperature	有Annealed	ASTM D-648	106	°C
Combustibility		UL 94	HB	CLASS
Vicat softening temperature		ASTM D-1525	118	°C
Hot deformation temperature	无Annealed	ASTM D-648	97	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.19
Shrinkage rate		ASTM D955	0.002-0.006	%
Shrinkage rate	Shrinkage rate		ASTM D-955	0.002-0.006	%
Transmittance rate		ASTM D-1003	93	%
Refractive index		ASTM D-542	1.49

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.