ABS/PBT NOVALLOY B BM5544 DAICEL JAPAN
252
- Unit Price:US$ 2,511 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:33MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:--
Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 155 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.2 mm | UL 94 | V-1 |
| 1.5 mm | UL 94 | V-0 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | Flow | ASTM D955 | 0.20 - 0.40 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface resistivity | Internal Method | 4.0E+2 ohms | |
| Volume resistivity | Internal Method | 1.0E+2 ohms·cm |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 to 120 °C | ||
| drying time | 3.0 to 5.0 hr | ||
| Temperature at the rear of the barrel | 190 to 230 °C | ||
| Temperature in the middle of the barrel | 220 to 240 °C | ||
| Temperature at the front of the material cylinder | 240 to 250 °C | ||
| Spray nozzle temperature | 230 to 250 °C | ||
| Mold temperature | 60 to 80 °C | ||
| Back pressure | 5.00 to 20.0 Mpa | ||
| Screw speed | 50 to 90 rpm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2 | 130 Mpa | |
| Bending modulus | ISO 178 | 11000 Mpa | |
| bending strength | ISO 178 | 205 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.