ABS/PBT BM5544 DAICEL JAPAN
NOVALLOY B
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | DAICEL JAPAN/BM5544 |
|---|---|---|---|
| bending strength | ISO 178 | 205 Mpa | |
| Flexural modulus | ISO 178 | 11000 Mpa | |
| tensile strength | ISO 527-2 | 130 Mpa |
| Electrical performance | Test Condition | Test Method | DAICEL JAPAN/BM5544 |
|---|---|---|---|
| Surface Resistivity | 内部方法 | 4.0E+2 ohms | |
| Volume resistivity | 内部方法 | 1.0E+2 ohms·cm |
| flammability | Test Condition | Test Method | DAICEL JAPAN/BM5544 |
|---|---|---|---|
| UL flame retardant rating | 1.2 mm | UL 94 | V-1 |
| 1.5 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | DAICEL JAPAN/BM5544 |
|---|---|---|---|
| Shrinkage rate | Flow | ASTM D955 | 0.20 - 0.40 % |
| Thermal performance | Test Condition | Test Method | DAICEL JAPAN/BM5544 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 155 °C |
| injection | Test Condition | Test Method | DAICEL JAPAN/BM5544 |
|---|---|---|---|
| drying time | 3.0 to 5.0 hr | ||
| screw speed | 50 to 90 rpm | ||
| Temperature in the middle of the barrel | 220 to 240 °C | ||
| Temperature at the rear of the barrel | 190 to 230 °C | ||
| drying temperature | 80 to 120 °C | ||
| Temperature at the front of the material cylinder | 240 to 250 °C | ||
| Back pressure | 5.00 to 20.0 Mpa | ||
| Temperature | 60 to 80 °C | ||
| Spray nozzle temperature | 230 to 250 °C |