PA66 Ultramid® A3X2G5 BASF GERMANY

519

Unit Price:US$ 5,060 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
74MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Electrical performance｜Flame retardant｜Oil resistant
Application Areas:Electrical applications｜Electrical components
Color:--
Grade:Flame retardant grade

Material Certification

SGS

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			玻纤增强注射级.红磷阻燃剂长期稳定性.具有优异的机械性能和电性能
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength		ASTM D256/ISO 179	13/17	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	3/4.5	%
Tensile modulus		ASTM D638/ISO 527	8500/6000	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	140/100	kg/cm²(MPa)[Lb/in²]
Fracture stress (V=50mm/min)	干/湿		140/100	Mpa
Tensile yield stress (V=50mm/min)	干/湿		140/100	Mpa
Charpy Notched Impact Strength	30℃，干		60	KJ/m
Bending modulus	干/湿		7100	Mpa
elongation	≤0.5%, +23℃，湿		3500	Mpa
Ball Pressure Test	干/湿		190	Mpa
Elongation at Break	干/湿，V=50mm/min		3/4.5	%
Charpy Notched Impact Strength	+23℃，干/湿		13/17	KJ/m
Impact strength of cantilever beam gap	+23℃，干/湿		11/17	KJ/m
Tensile modulus	干/湿		8500/6000	Mpa
Tensile creep modulus	1000h,湿		3500	Mpa
Elongation at Break	干/湿，V=50mm/min		3/4.5	%
impact strength	+23℃，干/湿		4/10	J
Charpy Notched Impact Strength	+23℃，干/湿		65/70	KJ/m
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	HDT	ASTM D648/ISO 75	250 1.8Mpa	℃（℉）
Melting temperature			260	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	2.5-3.5/6-8	mm/mm.℃
Hot deformation temperature	0.45MPa负荷，Dry		250	°C
Maximum operating temperature			220	°C
Linear coefficient of thermal expansion	（23-80）℃，Dry		2.5-3.5/6-8
thermal conductivity	Dry		0.27	W/(m.K)
Temperature index	在20000h/5000h，后拉伸强度下降50%时		139/157	°C
specific heat	Dry		1.5	J/(g.K)
Hot deformation temperature	1.8MPa负荷，Dry		250	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.34
Water absorption rate		ASTM D570/ISO 62	5.7-6.3	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257/IEC 60093	10^13/10^10	Ω
Volume resistivity		ASTM D257/IEC 60093	10^15/10^12	Ω.cm
Compared to the Leakage Traceability Index (CTI)	干/湿		CTI 525 M
Dielectric constant	1MHz，干/湿		3.7/5
Compared to the Leakage Traceability Index (CTI)	干/湿		CTI 500
Dielectric strength	K20/P50，干/湿		80/65	KV/mm
Volume resistivity	干/湿		10	Ω.cm
Surface resistivity	干/湿		>10	Ω
Loss angle	1MHz，干/湿		0.02/0.1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Weitai	US$ 5840 /MT
Dongguan Sharp Plastic	US$ 6420 /MT
Dongguan Juheng	US$ 6420 /MT

Supplier Join

Get App

Top

PA66 Ultramid® A3X2G5 BASF GERMANY

Material Description

Material Certification

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index