PEI LNP™ THERMOCOMP™ EC-1005 EM(EE005E-BK1A604) SABIC INNOVATIVE US
231
- Unit Price:US$ 22,601 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant|Carbon fiber reinforced
- Application Areas:Automotive components|Communication equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
impact performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Multi axis Instrumented Impact Energy | ISO 6603-2 | 3.00 J | |
Dart impact | 23°C,TotalEnergy | ASTM D3763 | 11.6 J |
23°C,EnergyatPeakLoad | ASTM D3763 | 10.4 J | |
Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 24 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.8 kJ/m² |
mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
bending strength | Break,50.0mmSpan | ASTM D790 | 274 Mpa |
Yield,50.0mmSpan | ASTM D790 | 275 Mpa | |
Bending modulus | ISO 178 | 16200 Mpa | |
50.0mmSpan | ASTM D790 | 16300 Mpa | |
Tensile strain | Break | ISO 527-2/5 | 1.4 % |
elongation | Break | ASTM D638 | 1.4 % |
tensile strength | Break | ISO 527-2/5 | 200 Mpa |
Break | ASTM D638 | 200 Mpa | |
Tensile modulus | ISO 527-2/1 | 18200 Mpa | |
ASTM D638 | 18300 Mpa |
thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Hot deformation temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 207 °C |
Linear coefficient of thermal expansion | MD:-30to30°C | ASTM D696 | 2.1E-05 cm/cm/°C |
MD:-40to40°C | ASTME831 | 1.9E-05 cm/cm/°C | |
MD:-40to40°C | ISO 11359-2 | 1.9E-05 cm/cm/°C | |
Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTM D648 | 204 °C |
0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 212 °C | |
0.45MPa,Unannealed,3.20mm | ASTM D648 | 210 °C | |
Linear coefficient of thermal expansion | TD:-30to30°C | ASTM D696 | 2.7E-05 cm/cm/°C |
TD:-40to40°C | ASTME831 | 2.7E-05 cm/cm/°C | |
TD:-40to40°C | ISO 11359-2 | 2.7E-05 cm/cm/°C |
Physical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.27 % |
24hr,50%RH | ASTM D570 | 0.17 % | |
Shrinkage rate | MD:24hr | ISO 294-4 | 0.10-0.30 % |
TD:24hr | ISO 294-4 | 0.30-0.50 % | |
TD:24hr | ASTM D955 | 0.50-0.70 % | |
MD:24hr | ASTM D955 | 0.070-0.090 % |
Electrical performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Surface resistivity | ASTM D257 | 1.0E+2to1.0E+5 ohms | |
Volume resistivity | ASTM D257 | 1.0E+2to1.0E+6 ohms·cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.