PEI EC-1005 EM(EE005E-BK1A604) SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Automotive components,Communication equipment
Flame retardant,Carbon fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/EC-1005 EM(EE005E-BK1A604) |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 24 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 11.6 J |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 3.00 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.8 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 10.4 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/EC-1005 EM(EE005E-BK1A604) |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 18200 Mpa | |
| ASTM D638 | 18300 Mpa | ||
| tensile strength | 断裂 | ISO 527-2/5 | 200 Mpa |
| elongation | 断裂 | ASTM D638 | 1.4 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 275 Mpa |
| Flexural modulus | ISO 178 | 16200 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 1.4 % |
| tensile strength | 断裂 | ASTM D638 | 200 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 16300 Mpa |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 274 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/EC-1005 EM(EE005E-BK1A604) |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.0E+2to1.0E+6 ohms·cm | |
| Surface Resistivity | ASTM D257 | 1.0E+2to1.0E+5 ohms |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/EC-1005 EM(EE005E-BK1A604) |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.10-0.30 % |
| MD：24小时 | ASTM D955 | 0.070-0.090 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.17 % |
| 平衡,23°C,50%RH | ISO 62 | 0.27 % | |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.50-0.70 % |
| TD:24小时 | ISO 294-4 | 0.30-0.50 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/EC-1005 EM(EE005E-BK1A604) |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 212 °C |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 2.1E-05 cm/cm/°C |
| TD：-40到40°C | ASTME831 | 2.7E-05 cm/cm/°C | |
| TD：-40到40°C | ISO 11359-2 | 2.7E-05 cm/cm/°C | |
| TD：-30to30°C | ASTM D696 | 2.7E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 210 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 1.9E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 1.9E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 207 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 204 °C |