PA66 Leona™ 1200S ASAHI JAPAN
179
- Unit Price:US$ 4,815 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:40MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜High rigidity
- Application Areas:Plastic accessories｜Laptop case｜consumables｜Automotive Applications
- Color:--
- Grade:High mobility
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 乾 | ASTM D648 | 70 °C 18.2kgf/cm |
| Linear coefficient of thermal expansion | 乾 | ASTM D696 | 8 1e-5/cm.°C |
| Heat Deflection Temperature | 乾 | ASTM D648 | 230 |
| UL flame retardant rating | Dry | UL 94 | V-2 |
| Combustibility (rate) | UL 94 | v-2 | |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 230 ℃（℉） |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 8 mm/mm.℃ |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 高流动 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 湿 | 2.5 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 乾 | 1.3-2.0 % | |
| density | ASTM D792/ISO 1183 | 1.14 | |
| shrinkage rate | ASTM D955 | 1.3-2.0 % | |
| Water absorption rate | ASTM D570/ISO 62 | 2.5 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257/IEC 60093 | 10*10 Ω.cm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 乾 | ASTM D638 | 780 Kgf/cm |
| bending strength | 乾 | ASTM D790 | 1200 Kgf/cm |
| (fracture) elongation rate | 湿 | ASTM D638 | 250 % |
| Taber wear resistance | 湿 | ASTM D1044 | 7 mg/1000次 |
| tensile strength | 湿 | ASTM D638 | 530 Kgf/cm |
| (fracture) elongation rate | 乾 | ASTM D638 | 50 % |
| Rockwell hardness | 湿 | ASTM D785 | 55/108 M/R |
| Impact strength of cantilever beam gap | 湿 | ASTM D256 | 14 Kgf.cm/cm |
| 乾 | ASTM D256 | 3.5 Kgf.cm/cm | |
| flexural modulus | 湿 | ASTM D790 | 12.000 Kgf/cm |
| Rockwell hardness | 乾 | ASTM D785 | 80/120 M/R |
| bending strength | 湿 | ASTM D790 | 550 Kgf/cm |
| flexural modulus | 乾 | ASTM D790 | 28.550 Kgf/cm |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 34 kg·cm/cm(J/M)ft·lb/in | |
| Elongation at break | ASTM D638/ISO 527 | 50 % | |
| tensile strength | ASTM D638/ISO 527 | 76.5 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | R120 | |
| flexural modulus | ASTM D790/ISO 178 | 2790 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 118 kg·cm/cm(J/M)ft·lb/in | |
| Elongation at break | ASTM D638/ISO 527 | - % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.