Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 1200S ASAHI JAPAN
Leona™
Plastic accessories,Laptop case,consumables,Automotive Applications
High mobility,High rigidity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/1200S |
|---|---|---|---|
| Water absorption rate | 湿 | 2.5 % |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/1200S |
|---|---|---|---|
| Taber wear resistance | 湿 | ASTM D1044 | 7 mg/1000次 |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 34 kg·cm/cm(J/M)ft·lb/in | |
| 乾 | ASTM D256 | 3.5 Kgf.cm/cm | |
| bending strength | 乾 | ASTM D790 | 1200 Kgf/cm |
| Flexural modulus | ASTM D790/ISO 178 | 2790 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 118 kg·cm/cm(J/M)ft·lb/in | |
| 湿 | ASTM D790 | 550 Kgf/cm | |
| elongation at break | ASTM D638/ISO 527 | - % | |
| (fracture) elongation rate | 乾 | ASTM D638 | 50 % |
| Rockwell hardness | ASTM D785 | R120 | |
| (fracture) elongation rate | 湿 | ASTM D638 | 250 % |
| Impact strength of cantilever beam gap | 湿 | ASTM D256 | 14 Kgf.cm/cm |
| tensile strength | ASTM D638/ISO 527 | 76.5 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | 湿 | ASTM D785 | 55/108 M/R |
| 乾 | ASTM D785 | 80/120 M/R | |
| tensile strength | 湿 | ASTM D638 | 530 Kgf/cm |
| 乾 | ASTM D638 | 780 Kgf/cm | |
| Flexural modulus | 湿 | ASTM D790 | 12.000 Kgf/cm |
| 乾 | ASTM D790 | 28.550 Kgf/cm |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/1200S |
|---|---|---|---|
| Volume resistivity | ASTM D257/IEC 60093 | 10*10 Ω.cm |
| other | Test Condition | Test Method | ASAHI JAPAN/1200S |
|---|---|---|---|
| characteristic | 高流动 |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/1200S |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 1.3-2.0 % | |
| density | ASTM D792/ISO 1183 | 1.14 | |
| Water absorption rate | ASTM D570/ISO 62 | 2.5 % |
| physical property | Test Condition | Test Method | ASAHI JAPAN/1200S |
|---|---|---|---|
| Shrinkage rate | 乾 | 1.3-2.0 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/1200S |
|---|---|---|---|
| Linear coefficient of thermal expansion | 乾 | ASTM D696 | 8 1e-5/cm.°C |
| Combustibility (rate) | UL 94 | v-2 | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 230 ℃（℉） |
| UL flame retardant rating | Dry | UL 94 | V-2 |
| Heat distortion temperature | 乾，HDT | ASTM D648 | 70 °C 18.2kgf/cm |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 8 mm/mm.℃ | |
| Heat distortion temperature | 乾，HDT | ASTM D648 | 230 |