Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced
- Application Areas:Casters｜Electrical applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 130 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 123 °C | |
| vicat | ISO 306/B50 | 134 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 5E-05 cm/cm/°C |
| TD | ISO 11359-2 | 6E-05 cm/cm/°C | |
| RTI Elec | 1.7mm | UL 746 | 130 °C |
| RTI Imp | 1.7mm | UL 746 | 120 °C |
| RTI Str | 1.7mm | UL 746 | 130 °C |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 123 ℃（℉） |
| vicat | ASTM D1525/ISO R306 | 134 ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 0.5 mm/mm.℃ |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL 94 | HB |
| 1.7mm | UL 94 | V-2 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 55 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | TD:4.00mm | 内部方法 | 0.40-0.60 % |
| MD:4.00mm | 内部方法 | 0.35-0.55 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.16 % |
| density | ASTM D792/ISO 1183 | 1270 | |
| shrinkage rate | ASTM D955 | 0.35-0.55 % | |
| Water absorption rate | ASTM D570/ISO 62 | 0.16 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.20 |
| 1MHz | IEC 60250 | 3.20 | |
| Dissipation Factor | 100Hz | IEC 60250 | 1E-03 |
| 1MHz | IEC 60250 | 9E-03 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3000 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 65.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/5 | 5.0 % |
| flexural modulus | ISO 178 | 3100 Mpa | |
| bending strength | ISO 178 | 110 Mpa | |
| Elongation at break | ASTM D638/ISO 527 | 5.0 % | |
| Tensile modulus | ASTM D638/ISO 527 | 3000 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 3100 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 110 kg/cm²(MPa)[Lb/in²] |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.