PC G-3110PH TEIJIN JAPAN
PANLITE®
Casters、Electrical applications
Flame retardant、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | TEIJIN JAPAN/G-3110PH |
---|---|---|---|
Impact strength of simply supported beam without notch | ISO 179 | 55 kJ/m² |
Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/G-3110PH |
---|---|---|---|
Tensile modulus | ISO 527-2/1 | 3000 Mpa | |
bending strength | ASTM D790/ISO 178 | 110 kg/cm²(MPa)[Lb/in²] | |
tensile strength | 断裂 | ISO 527-2/5 | 65.0 Mpa |
Flexural modulus | ASTM D790/ISO 178 | 3100 kg/cm²(MPa)[Lb/in²] | |
bending strength | ISO 178 | 110 Mpa | |
Flexural modulus | ISO 178 | 3100 Mpa | |
Tensile strain | 断裂 | ISO 527-2/5 | 5.0 % |
Tensile modulus | ASTM D638/ISO 527 | 3000 kg/cm²(MPa)[Lb/in²] | |
elongation at break | ASTM D638/ISO 527 | 5.0 % |
Electrical performance | Test Condition | Test Method | TEIJIN JAPAN/G-3110PH |
---|---|---|---|
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
dielectric strength | IEC 60243-1 | 35 KV/mm | |
Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
relative permittivity | 100Hz | IEC 60250 | 3.20 |
Dissipation Factor | 100Hz | IEC 60250 | 1E-03 |
relative permittivity | 1MHz | IEC 60250 | 3.20 |
Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
Dissipation Factor | 1MHz | IEC 60250 | 9E-03 |
Physical properties | Test Condition | Test Method | TEIJIN JAPAN/G-3110PH |
---|---|---|---|
Shrinkage rate | ASTM D955 | 0.35-0.55 % | |
density | ASTM D792/ISO 1183 | 1270 | |
Water absorption rate | ASTM D570/ISO 62 | 0.16 % |
flammability | Test Condition | Test Method | TEIJIN JAPAN/G-3110PH |
---|---|---|---|
UL flame retardant rating | 1.7mm | UL 94 | V-2 |
0.40mm | UL 94 | HB |
physical property | Test Condition | Test Method | TEIJIN JAPAN/G-3110PH |
---|---|---|---|
Water absorption rate | 23°C,24hr | ISO 62 | 0.16 % |
Shrinkage rate | MD:4.00mm | 内部方法 | 0.35-0.55 % |
TD:4.00mm | 内部方法 | 0.40-0.60 % |
Thermal performance | Test Condition | Test Method | TEIJIN JAPAN/G-3110PH |
---|---|---|---|
Heat distortion temperature | HDT | ASTM D648/ISO 75 | 123 ℃(℉) |
vicat | ASTM D1525/ISO R306 | 134 ℃(℉) | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 130 °C |
RTI Imp | 1.7mm | UL 746 | 120 °C |
vicat | ISO 306/B50 | 134 °C | |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 123 °C |
RTI Elec | 1.7mm | UL 746 | 130 °C |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 5E-05 cm/cm/°C |
RTI Str | 1.7mm | UL 746 | 130 °C |
Linear coefficient of thermal expansion | TD | ISO 11359-2 | 6E-05 cm/cm/°C |
ASTM D696/ISO 11359 | 0.5 mm/mm.℃ |