PC IUPILON™ EFR3000 BK MITSUBISHI ENGINEERING JAPAN

Unit Price:US$ 2,810 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
31MT
Delivery Terms:
FOB
Port of Loading :
Shenzhen Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Guangdong Zecheng New Material Technology Co., Ltd.

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜Flame retardant
Application Areas:Non specific food
Color:--
Grade:Injection grade

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			非溴非磷阻燃不透明
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak
machinability	Test Condition	Test Method	Test Result	Test Unit
Dry conditions			热风干燥 120℃---約4-8小时
Processing temperature			250-280	°C
	Processing temperature			270-300	°C
	Processing temperature	Processing temperature			260-290	°C
Screw speed			50-100	rpm
Mold temperature			70-100	°C
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.0mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638/ISO 527	2300	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2500	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	92	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	67	%
Tensile modulus		ISO 527-2	2300	Mpa
tensile strength	Yield	ISO 527-2	61.0	Mpa
Tensile strain	Yield	ISO 527-2	4.7	%
Nominal tensile fracture strain		ISO 527-2	67	%
Bending modulus		ISO 178	2500	Mpa
bending strength		ISO 178	92.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility (rate)		UL 94	V-0 (1.0mm)
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	6.6E-05	mm/mm.℃
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	137	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	125	°C
Linear coefficient of thermal expansion	TD	ISO 11359-2	6.7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	6.6E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.19
Shrinkage rate		ASTM D955	0.5 - 0.7	%
Water absorption rate		ASTM D570/ISO 62	0.24	%
melt mass-flow rate	300°C/1.2kg	ISO 1133	22	g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	21.0	cm3/10min
Shrinkage rate	TD:3.20mm		0.50-0.70	%
	Shrinkage rate	MD:3.20mm		0.50-0.70	%
	Shrinkage rate	Shrinkage rate	吸水率(Saturation,23°C)		0.24	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257/IEC 60093	6.E+15	Ω
Dielectric constant		ASTM D150/IEC 60250	3.1
Volume resistivity		ASTM D257/IEC 60093	3.E+14	Ω.cm
Dissipation factor	1MHz	IEC 60250	9E-03
Dissipation factor	Dissipation factor	100Hz	IEC 60250	6E-04
Relative permittivity	1MHz	IEC 60250	3.10
Relative permittivity	Relative permittivity	100Hz	IEC 60250	3.10
Dielectric strength	3.00mm	IEC 60243-1	18	KV/mm
Dielectric strength	Dielectric strength	1.00mm	IEC 60243-1	31	KV/mm
Volume resistivity		IEC 60093	3E+16	ohms·cm
Surface resistivity		IEC 60093	6E+15	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
ASIAPLAS	US$ 3610 /MT

Supplier Join

Get App

Top

PC IUPILON™ EFR3000 BK MITSUBISHI ENGINEERING JAPAN

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index