Material Properties:Glass fiber reinforced｜High rigidity｜High temperature resistance
Application Areas:Household appliances｜Household appliances｜Automotive sector｜Electrical field｜Electronic field｜Switch panel｜Engine hood parts｜Laptop case
Color:--
Grade:Injection grade

Material Certification

MSDS

Technical Data Sheet Compare

other	Test Condition	Test Method	Test Result
characteristic			超高耐热.高温刚性.玻璃纤维.标准
Color			VF2001/BK010P

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	HDT	ASTM D648/ISO 75	340 ℃（℉）
	Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	340 °C
	Heat Deflection Temperature	Heat Deflection Temperature	8.0MPa,未退火	ISO 75-2/C	267 °C
melting temperature		ISO 11357-3	350 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1E-06 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	2.3E-05 cm/cm/°C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0

Impact resistance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	14 kJ/m²

Electrical performance	Test Condition	Test Method	Test Result
arc resistance		ASTM D495/IEC 60112	138
Surface Resistivity		IEC 60093	1E+17 ohms
volume resistivity		IEC 60093	1E+17 ohms·cm
dielectric strength		IEC 60243-1	37 KV/mm
relative permittivity	1MHz	IEC 60250	3.50
Dissipation Factor	1MHz	IEC 60250	9E-03

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.66
shrinkage rate	TD	ISO 294-4	0.40 %
shrinkage rate	shrinkage rate	MD	ISO 294-4	0.10 %
Water absorption rate	饱和,23°C	ISO 62	4E-03 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	7E-03 %

mechanical properties	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ASTM D256/ISO 179	12 kg·cm/cm(J/M)ft·lb/in
tensile strength		ASTM D638/ISO 527	155 kg/cm²(MPa)[Lb/in²]
flexural modulus		ASTM D790/ISO 178	16000 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	220 kg/cm²(MPa)[Lb/in²]
Tensile modulus		ISO 527-2/1A/1	15500 Mpa
tensile strength	断裂	ISO 527-2/1A/5	140 Mpa
Tensile strain	断裂	ISO 527-2/1A/5	1.3 %
flexural modulus	23°C	ISO 178	14500 Mpa
bending strength	23°C	ISO 178	230 Mpa
Compressive Stress	1%Strain	ISO 604	114 Mpa
Fracture bending strain		ISO 178	2.0 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.