Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP S135 JAPAN POLYPLASTIC
LAPEROS®
Household appliances,Household appliances,Automotive sector,Electrical field,Electronic field,Switch panel,Engine hood parts,Laptop case
Glass fiber reinforced,High rigidity,High temperature resistan
UL
MSDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JAPAN POLYPLASTIC/S135 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 14 kJ/m² |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/S135 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 37 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+17 ohms·cm | |
| arc resistance | ASTM D495/IEC 60112 | 138 | |
| relative permittivity | 1MHz | IEC 60250 | 3.50 |
| Surface Resistivity | IEC 60093 | 1E+17 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 9E-03 |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/S135 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 220 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 16000 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2/1A/1 | 15500 Mpa | |
| bending strength | 23°C | ISO 178 | 230 Mpa |
| Flexural modulus | 23°C | ISO 178 | 14500 Mpa |
| Compressive Stress | 1%Strain | ISO 604 | 114 Mpa |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 12 kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 140 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.3 % |
| Fracture bending strain | ISO 178 | 2.0 % | |
| tensile strength | ASTM D638/ISO 527 | 155 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | JAPAN POLYPLASTIC/S135 |
|---|---|---|---|
| characteristic | 超高耐热.高温刚性.玻璃纤维.标准 | ||
| Color | VF2001/BK010P |
| Physical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/S135 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.66 |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/S135 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/S135 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.40 % |
| MD | ISO 294-4 | 0.10 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 7E-03 % |
| 饱和,23°C | ISO 62 | 4E-03 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/S135 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 350 °C | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 340 ℃（℉） |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 340 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1E-06 cm/cm/°C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 267 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 2.3E-05 cm/cm/°C |