ABS/PA SCHULABLEND® M/MK 8 A SCHULMAN USA

422

Unit Price:US$ 2,542 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
62MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Filler: Glass fiber reinforced material｜8.0% filler by weight｜20% filler by weight
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	70 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	36 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	IEC 60695-11-10,-20	HB
Burning rate		ISO 3795	<100 mm/min
Flammability level	1.5mm	IEC 60695-11-10,-20	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1A/1	3300 Mpa
tensile strength	Yield	ISO 527-2/1A/50	43.0 Mpa
Tensile strain	Yield	ISO 527-2/1A/50	3.0 %
Tensile modulus		ISO 527-2/1A/1	4900 Mpa
tensile strength	Break	ISO 527-2/1A/5	77.0 Mpa
Tensile strain	Break	ISO 527-2/1A/5	4.5 %

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	152 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	76.0 °C
Vicat softening temperature	--	ISO 306/A50	190 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	115 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	179 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	101 °C
Vicat softening temperature	--	ISO 306/A50	213 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	128 °C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	250°C/5.0kg	ISO 1133	4.00 cm3/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	250°C/5.0kg	ISO 1133	2.00 cm3/10min

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	>1.0E+13 ohms·cm

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H358/30	ISO 2039-1	93.0 Mpa
Ball Pressure Test	Ball Pressure Test	H358/30	ISO 2039-1	97.0 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS/PA SCHULABLEND® M/MK 8 A SCHULMAN USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet