PPA

PPA AMODEL® AT-1002 HS SOLVAY USA

320

Unit Price:US$ 8,492 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
35MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜Thermal stability
Application Areas:Industrial applications｜Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	TotalEnergy	ASTM D3763	54.2 J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	NoBreak
Puncture intensity		ASTM D3763	4448 N
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ASTM D790	2210 Mpa
Bending modulus	Bending modulus	23°C	ISO 178	2280 Mpa
Tensile modulus		ASTM D638	2760 Mpa
shear strength		ASTM D732	64.1 Mpa
bending strength	100°C	ISO 178	49.6 Mpa
Bending modulus	100°C	ISO 178	1720 Mpa
bending strength		ASTM D790	103 Mpa
bending strength	bending strength	23°C	ISO 178	79.3 Mpa
Tensile strain	Yield,100°C	ISO 527-2	3.7 %
elongation	Break	ASTM D638	80 %
Tensile strain	Break,23°C	ISO 527-2	15 %
tensile strength		ASTM D638	83.4 Mpa
	tensile strength	Yield,23°C	ISO 527-2	75.2 Mpa
		tensile strength	Yield,100°C	ISO 527-2	38.6 Mpa
		tensile strength	tensile strength	Break,23°C	ISO 527-2	68.3 Mpa
Tensile strain	Yield,23°C	ISO 527-2	5.0 %
Tensile modulus	23°C	ISO 527-2	2760 Mpa
Tensile modulus	Tensile modulus	100°C	ISO 527-2	2100 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Annealed	ASTM D648	121 °C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	118 °C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Annealed	ASTM D648	163 °C
Linear coefficient of thermal expansion	TD：100to200°C	ASTME831	1.4E-04 cm/cm/°C
	Linear coefficient of thermal expansion	TD：0to100°C	ASTME831	9.3E-05 cm/cm/°C
		Linear coefficient of thermal expansion	MD：100to200°C	ASTME831	1.3E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：0to100°C	ASTME831	7.8E-05 cm/cm/°C
Melting temperature		ISO 11357-3	315 °C
Melting temperature	Melting temperature		ASTM D3418	315 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	24hr	ASTM D570	0.50 %
Shrinkage rate	TD	ASTM D955	2.1 %
Shrinkage rate	Shrinkage rate	MD	ASTM D955	2.0 %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric strength		ASTM D149	17 KV/mm
Volume resistivity		ASTM D257	1.2E+16 ohms·cm
Surface resistivity		ASTM D257	8E+13 ohms
High voltage arc tracing rate	HVTR	UL 746	mm/min
Compared to the anti leakage trace index		ASTM D3638	PLC 0
Dielectric constant	60Hz	ASTM D150	3.30
Dielectric constant	Dielectric constant	1MHz	ASTM D150	3.30
Dissipation factor	60Hz	ASTM D150	4E-03
Dissipation factor	Dissipation factor	1MHz	ASTM D150	0.016

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPA AMODEL® AT-1002 HS SOLVAY USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet