Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PPA AT-1002 HS SOLVAY USA
AMODEL®
Industrial applications、Automotive Applications
High temperature resistan、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SOLVAY USA/AT-1002 HS |
---|---|---|---|
Puncture Strength | ASTM D3763 | 4448 N | |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
Dart impact | TotalEnergy | ASTM D3763 | 54.2 J |
Mechanical properties | Test Condition | Test Method | SOLVAY USA/AT-1002 HS |
---|---|---|---|
tensile strength | Yield,100°C | ISO 527-2 | 38.6 Mpa |
bending strength | ASTM D790 | 103 Mpa | |
Flexural modulus | 100°C | ISO 178 | 1720 Mpa |
Tensile modulus | 23°C | ISO 527-2 | 2760 Mpa |
tensile strength | 断裂,23°C | ISO 527-2 | 68.3 Mpa |
Flexural modulus | ASTM D790 | 2210 Mpa | |
Tensile modulus | 100°C | ISO 527-2 | 2100 Mpa |
tensile strength | ASTM D638 | 83.4 Mpa | |
bending strength | 100°C | ISO 178 | 49.6 Mpa |
Tensile modulus | ASTM D638 | 2760 Mpa | |
elongation | 断裂 | ASTM D638 | 80 % |
Tensile strain | 断裂,23°C | ISO 527-2 | 15 % |
bending strength | 23°C | ISO 178 | 79.3 Mpa |
tensile strength | 屈服,23°C | ISO 527-2 | 75.2 Mpa |
Flexural modulus | 23°C | ISO 178 | 2280 Mpa |
Tensile strain | Yield,100°C | ISO 527-2 | 3.7 % |
屈服,23°C | ISO 527-2 | 5.0 % | |
shear strength | ASTM D732 | 64.1 Mpa |
Electrical performance | Test Condition | Test Method | SOLVAY USA/AT-1002 HS |
---|---|---|---|
Dissipation Factor | 60Hz | ASTM D150 | 4E-03 |
dielectric constant | 60Hz | ASTM D150 | 3.30 |
High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | mm/min |
Volume resistivity | ASTM D257 | 1.2E+16 ohms·cm | |
Compared to the Leakage Tracking Index (CTI) | ASTM D3638 | PLC 0 | |
Surface Resistivity | ASTM D257 | 8E+13 ohms | |
Dissipation Factor | 1MHz | ASTM D150 | 0.016 |
dielectric strength | ASTM D149 | 17 KV/mm | |
dielectric constant | 1MHz | ASTM D150 | 3.30 |
flammability | Test Condition | Test Method | SOLVAY USA/AT-1002 HS |
---|---|---|---|
UL flame retardant rating | UL 94 | HB |
physical property | Test Condition | Test Method | SOLVAY USA/AT-1002 HS |
---|---|---|---|
Shrinkage rate | MD | ASTM D955 | 2.0 % |
Water absorption rate | 24hr | ASTM D570 | 0.50 % |
Shrinkage rate | TD | ASTM D955 | 2.1 % |
Thermal performance | Test Condition | Test Method | SOLVAY USA/AT-1002 HS |
---|---|---|---|
Linear coefficient of thermal expansion | TD:100到200°C | ASTME831 | 1.4E-04 cm/cm/°C |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/Af | 118 °C |
melting temperature | ISO 11357-3 | 315 °C | |
Heat distortion temperature | 1.8MPa,退火,HDT | ASTM D648 | 121 °C |
Linear coefficient of thermal expansion | MD:100到200°C | ASTME831 | 1.3E-04 cm/cm/°C |
TD:0to100°C | ASTME831 | 9.3E-05 cm/cm/°C | |
melting temperature | ASTM D3418 | 315 °C | |
Heat distortion temperature | 0.45MPa,退火,HDT | ASTM D648 | 163 °C |
Linear coefficient of thermal expansion | MD:0to100°C | ASTME831 | 7.8E-05 cm/cm/°C |