PBT VALOX™ 357X BK SABIC INNOVATIVE US
187
- Unit Price:US$ 3,744 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜UV resistance
- Application Areas:Electrical appliances｜Plastic bag｜Casters｜Household goods
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 115 |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 115 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Flow: -40 to 40 ° C | ASTME831 | 9.2E-05 cm/cm/°C | |
| Flow: 23 to 80 ° C | 23到80℃ | ISO 11359-2 | 1E-04 cm/cm/°C |
| Horizontal: -40 to 40 ° C | 横向, -40到40℃ | ASTME831 | 8.4E-05 cm/cm/°C |
| Horizontal: 23 to 80 ° C | 横向, 23到80℃ | ISO 11359-2 | 1E-04 cm/cm/°C |
| thermal conductivity | ISO 8302 | 0.17 W/m/K | |
| RTI Elec | UL 746 | 120 °C | |
| 0.45MPa, Unanealed, 3.20mm | ASTM D648 | 130 °C | |
| 0.45MPa, Unanealed, 100mm span | ISO 75-2/Be | 135 °C | |
| 0.45MPa, Unanealed, 64.0mm span | ISO 75-2/Bf | 130 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 85.0 °C | |
| 1.8MPa, Unanealed, 100mm span | ISO 75-2/Ae | 85.0 °C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 85.0 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI | UL 746 | 140 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.750mm | UL 94 | V-0 |
| 2.50mm | UL 94 | 5VA | |
| Burning wire flammability index | 1.00mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | ISO 4589-2 | 30 % |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt viscosity | 260°C,1500sec^-1 | ISO 11443 | 310 Pa·s |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 23°C | ISO 180/1A | 40 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ASTMD4812 | 无断裂 |
| 23°C | ASTMD4812 | 无断裂 | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 35.0 J |
| -30°C | ISO 179/1eA | 20 kJ/m² | |
| 23°C | ISO 179/1eA | 45 kJ/m² | |
| ISO 179/2C | 40 kJ/m² | ||
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 | |
| -30°C | ASTM D256 | 150 J/m | |
| 0°C | ASTM D256 | 190 J/m | |
| 23°C | ASTM D256 | 500 J/m | |
| -30°C | ISO 180/1A | 10 kJ/m² | |
| 0°C | ISO 180/1A | 20 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 250°C/5.0kg | ASTM D1238 | 9.6 g/10min |
| 265°C/5.0kg | ASTM D1238 | 13 g/10min | |
| 266°C/5.0kg | ASTM D1238 | 13 g/10min | |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 8.00 cm3/10min |
| 265°C/5.0kg | ISO 1133 | 10.0 cm3/10min | |
| shrinkage rate | MD1 | 内部方法 | 1.1-1.8 % |
| MD:3.20mm | 内部方法 | 1.0-1.4 % | |
| TD2 | 内部方法 | 0.90-1.8 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.50 % |
| 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| 50Hz | 50Hz | IEC 60250 | 3.00 |
| 60Hz | 60Hz | IEC 60250 | 3.00 |
| 1MHz | 1MHz | ASTM D150 | 0.013 |
| 50Hz | 50Hz | IEC 60250 | 2E-03 |
| 60Hz | 60Hz | IEC 60250 | 2E-03 |
| 1MHz | 1MHz | IEC 60250 | 1.3E-03 |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| -- | IEC 60112 | PLC 3 | |
| 解决方案B | IEC 60112 | PLC 4 | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | ASTMD257 | >1.0E+15 ohms·cm | |
| 16mm, inoyl | ASTM D149 | 25 KV/mm | |
| 3.20mm, inoil | ASTM D149 | 17 KV/mm | |
| 0.800mm, In oil | IEC 60243-1 | 34 KV/mm | |
| 1.60mm, In oil | IEC 60243-1 | 25 KV/mm | |
| 3.20mm, In oil | IEC 60243-1 | 17 KV/mm | |
| 1MHz | 1MHz | ASTMD150 | 3.00 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| fracture | ISO 527-2/50 | 40.0 Mpa | |
| yield | ASTM D638 | 5.0 % | |
| ISO 527-2/50 | 5.0 % | ||
| fracture | ASTM D638 | 30 % | |
| ISO 527-2/50 | 30 % | ||
| 50.0mm span | ASTM D790 | 2100 Mpa | |
| --9 | ISO 178 | 2000 Mpa | |
| --10 | ISO 178 | 80.0 Mpa | |
| Yield, 50.0mm span | ASTM D790 | 78.0 Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 33.0 mg |
| --3 | ASTM D638 | 2000 Mpa | |
| yield | ASTM D638 | 50.0 Mpa | |
| ISO 527-2/50 | 50.0 Mpa | ||
| fracture | ASTM D638 | 40.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.