Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 357X BK SABIC INNOVATIVE US
VALOX™ 
Electrical appliances,Plastic bag,Casters,Household goods
Flame retardant,UV resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/357X BK
23°CISO 180/1A40 kJ/m²
Dart impact23°C,TotalEnergyASTM D376335.0 J
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
23°CISO 179/1eU无断裂
-30°CASTM D256150 J/m
ISO 179/1eA20 kJ/m²
Suspended wall beam without notch impact strength-30°CASTMD4812无断裂
23°CISO 179/1eA45 kJ/m²
0°CASTM D256190 J/m
23°CASTM D256500 J/m
Suspended wall beam without notch impact strength23°CASTMD4812无断裂
23°CISO 179/2C40 kJ/m²
-30°CISO 180/1A10 kJ/m²
0°CISO 180/1A20 kJ/m²
hardnessTest ConditionTest MethodSABIC INNOVATIVE US/357X BK
Rockwell hardnessR计秤ISO 2039-2115
ball-indentation hardnessH358/30ISO 2039-1115 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/357X BK
1.60mm, In oilIEC 60243-125 KV/mm
Volume resistivityASTMD257>1.0E+15 ohms·cm
High arc combustion index (HAI)HAIUL 746PLC 0
1MHz1MHzASTM D1500.013
3.20mm, In oilIEC 60243-117 KV/mm
60Hz60HzIEC 602502E-03
50Hz50HzIEC 602502E-03
Compared to the Leakage Tracking Index (CTI)解决方案BIEC 60112PLC 4
--IEC 60112PLC 3
0.800mm, In oilIEC 60243-134 KV/mm
High Voltage Arc Traceability Rate (HVTR)HVTRUL 746PLC 3
1MHz1MHzIEC 602501.3E-03
Hot wire ignition (HWI)HWIUL 746PLC 3
arc resistanceASTM D495PLC6
16mm, inoylASTM D14925 KV/mm
Surface ResistivityIEC 60093>1.0E+15 ohms
3.20mm, inoilASTM D14917 KV/mm
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 3
1MHz1MHzASTMD1503.00
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/357X BK
yieldASTM D6385.0 %
ASTM D63850.0 Mpa
Yield, 50.0mm spanASTM D79078.0 Mpa
yieldISO 527-2/5050.0 Mpa
--3ASTM D6382000 Mpa
fractureISO 527-2/5040.0 Mpa
ASTM D63840.0 Mpa
--10ISO 17880.0 Mpa
fractureISO 527-2/5030 %
ASTM D63830 %
yieldISO 527-2/505.0 %
--9ISO 1782000 Mpa
Taber abraser1000Cycles,1000g,CS-17转轮内部方法33.0 mg
50.0mm spanASTM D7902100 Mpa
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/357X BK
UL flame retardant rating0.750mmUL 94V-0
2.50mmUL 945VA
Burning wire flammability index1.00mmIEC 60695-2-12960 °C
Limiting Oxygen IndexISO 4589-230 %
Filling analysisTest ConditionTest MethodSABIC INNOVATIVE US/357X BK
melt viscosity260°C,1500sec^-1ISO 11443310 Pa·s
physical property Test ConditionTest MethodSABIC INNOVATIVE US/357X BK
melt mass-flow rate265°C/5.0kgASTM D123813 g/10min
Shrinkage rateTD2内部方法0.90-1.8 %
MD:3.20mm内部方法1.0-1.4 %
melt mass-flow rate266°C/5.0kgASTM D123813 g/10min
Melt volume flow rate250°C/5.0kgISO 11338.00 cm3/10min
Water absorption rate平衡,23°C,50%RHISO 620.15 %
饱和,23°CISO 620.50 %
Melt volume flow rate265°C/5.0kgISO 113310.0 cm3/10min
melt mass-flow rate250°C/5.0kgASTM D12389.6 g/10min
Shrinkage rateMD1内部方法1.1-1.8 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/357X BK
Horizontal: 23 to 80 ° C横向, 23到80℃ISO 11359-21E-04 cm/cm/°C
Flow: -40 to 40 ° CASTME8319.2E-05 cm/cm/°C
1.8MPa, Unanealed, 100mm spanISO 75-2/Ae85.0 °C
RTIUL 746140 °C
0.45MPa, Unanealed, 3.20mmASTM D648130 °C
Flow: 23 to 80 ° C23到80℃ISO 11359-21E-04 cm/cm/°C
thermal conductivityISO 83020.17 W/m/K
0.45MPa, Unanealed, 100mm spanISO 75-2/Be135 °C
Horizontal: -40 to 40 ° C横向, -40到40℃ASTME8318.4E-05 cm/cm/°C
0.45MPa, Unanealed, 64.0mm spanISO 75-2/Bf130 °C
1.8MPa, Unanealed, 64.0mm spanISO 75-2/Af85.0 °C
RTI ImpUL 746120 °C
1.8MPa, Unanealed, 3.20mmASTM D64885.0 °C
ball-indentation hardness125°CIEC 60695-10-2Pass
RTI ElecUL 746120 °C