PEI ULTEM™ HU1000 2H4D342 SABIC INNOVATIVE US
222
- Unit Price:US$ 13,541 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Middle flow｜Biocompatibility｜Steam sterilization
- Application Areas:Medical devices｜Medical and nursing supplies
- Color:--
- Grade:--
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTM D648 | 201 °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 215 °C | |
| vicat | ASTM D152510 | 219 °C | |
| -- | ISO 306/B50 | 215 °C | |
| -- | ISO 306/B120 | 211 °C | |
| Linear coefficient of thermal expansion | MD：-20to150°C | ASTME831 | 5.6E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 5E-05 cm/cm/°C | |
| TD：-20to150°C | ASTME831 | 5.4E-05 cm/cm/°C | |
| TD：-40到40°C | ISO 11359-2 | 5E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | ASTM D2863 | 47 % | |
| NBSSmokeDensity-Flaming,Ds,4min | ASTME662 | 0.700 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.0 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.0 kJ/m² |
| 23°C | ISO 180/1A | 6.0 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 9.0 g/10min |
| Melt volume flow rate | 220°C/5.0kg | ISO 1133 | 13.0 cm3/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 24hr | ASTM D570 | 0.25 % |
| 饱和,23°C | ISO 62 | 1.3 % | |
| 平衡,23°C | ASTM D570 | 1.3 % | |
| 平衡,23°C,50%RH | ISO 62 | 0.70 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| arc resistance | ASTM D495 | PLC 5 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 3 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 1 |
| volume resistivity | ASTM D257 | 1E+17 ohms·cm | |
| dielectric strength | 1.60mm,inAir | ASTM D149 | 33 KV/mm |
| 1.60mm,在油中 | ASTM D149 | 28 KV/mm | |
| dielectric constant | 1kHz | ASTM D150 | 3.15 |
| Dissipation Factor | 1kHz | ASTM D150 | 1.3E-03 |
| 2.45GHz | ASTM D150 | 2.5E-03 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2/5 | 85.0 Mpa |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 6.0 % |
| elongation | 断裂 | ASTM D638 | 60 % |
| Tensile strain | 断裂 | ISO 527-2/5 | 60 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 3440 Mpa |
| ISO 178 | 3300 Mpa | ||
| bending strength | ISO 178 | 160 Mpa | |
| 屈服,50.0mm跨距 | ASTM D790 | 173 Mpa | |
| Tensile modulus | ASTM D638 | 3580 Mpa | |
| ISO 527-2/1 | 3200 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 110 Mpa |
| 屈服 | ISO 527-2/5 | 105 Mpa | |
| 断裂 | ASTM D638 | 90.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.