ABS

ABS POLYLAC® PA-709S TAIWAN CHIMEI

429

Unit Price:US$ 2,065 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
254.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance
Application Areas:furniture｜container
Color:--
Grade:Extrusion grade

Material Certification

MSDS

RoHS

SGS

Technical Data Sheet

other	Test Condition	Test Method	Test Result
remarks			在射出周期中勿将热融胶长期停留在加热管中
characteristic			超高耐冲击
Color			--
purpose			挤出管材 / 家具 / 大件容器等

machinability	Test Condition	Test Method	Test Result
Dry conditions			80°C下烘料约2-3小时
Processing temperature			190-210 °C
	Processing temperature			220-250 °C °C
		Processing temperature			210-240 °C
		Processing temperature	Processing temperature			190-250°C °C
Screw speed			-- rpm
Mold temperature			-- °C
Melt Temperature			-- °C
pressure			-- Mpa

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTM D256/ISO 179	37（6.9） kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	-- %
Tensile modulus		ASTM D638/ISO 527	-- kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	370（5250） kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	40 %
Rockwell hardness		ASTM D785	R-100
Bending modulus		ASTM D790/ISO 178	20000（28000） kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	560（8000） kg/cm²(MPa)[Lb/in²]
Charpy Notched Impact Strength		ASTM D256/ISO 179	-- kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap		ASTM D256/ISO 179	-- kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	44（8.1） kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	-- %

thermal performance	Test Condition	Test Method	Test Result
Combustibility (rate)		UL 94	1.6mmHB
Hot deformation temperature	HDT	ASTM D648/ISO 75	96（205） ℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	86（187） ℃（℉）
Vicat softening temperature		ASTM D1525/ISO R306	-- ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	-- mm/mm.℃

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.03
Shrinkage rate		ASTM D955	-- %
Water absorption rate		ASTM D570/ISO 62	-- %
melt mass-flow rate		ASTM D1238/ISO 1133	0.4 g/10min
melt mass-flow rate	melt mass-flow rate		ASTM D1238/ISO 1133	4.5 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.