Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS PA-709S TAIWAN CHIMEI
POLYLAC®
furniture、container
High impact resistance
UL
MSDS
RoHS
SGS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TAIWAN CHIMEI/PA-709S |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 44（8.1） kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 560（8000） kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 20000（28000） kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 40 % | |
| Tensile modulus | ASTM D638/ISO 527 | -- kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | -- kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | -- % | |
| Rockwell hardness | ASTM D785 | R-100 | |
| tensile strength | ASTM D638/ISO 527 | 370（5250） kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | TAIWAN CHIMEI/PA-709S |
|---|---|---|---|
| characteristic | 超高耐冲击 | ||
| notes | 在射出周期中勿将热融胶长期停留在加热管中 | ||
| Color | -- | ||
| purpose | 挤出管材 / 家具 / 大件容器等 |
| Physical properties | Test Condition | Test Method | TAIWAN CHIMEI/PA-709S |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | -- % | |
| density | ASTM D792/ISO 1183 | 1.03 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 4.5 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | -- % |
| processability | Test Condition | Test Method | TAIWAN CHIMEI/PA-709S |
|---|---|---|---|
| process temperature | 190-250°C °C | ||
| pressure | -- Mpa | ||
| Dry conditions | 80°C下烘料约2-3小时 | ||
| screw speed | -- rpm | ||
| Melt Temperature | -- °C | ||
| Temperature | -- °C |
| Thermal performance | Test Condition | Test Method | TAIWAN CHIMEI/PA-709S |
|---|---|---|---|
| Combustibility (rate) | UL 94 | 1.6mmHB | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 86（187） ℃（℉） |
| vicat | ASTM D1525/ISO R306 | -- ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | -- mm/mm.℃ |