PBT

PBT VALOX™ 310SEO-1001 SABIC INNOVATIVE THAILAND

246

Unit Price:US$ 3,240 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
33MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:Industrial applications｜Electrical field｜Electronic field｜Switch panel｜Shell
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	23°C	ASTM D4812	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C9	ISO 180/1U	无断裂
Dart impact	23°C, Total Energy	ASTM D3763	200 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.71 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960 °C
Extreme Oxygen Index		ISO 4589-2	30 %

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	50.0 mm Span5	ASTM D790	2620 Mpa
elongation	Break	ISO 527-2/50	18 %
	elongation	Break4	ASTM D638	18 %
		elongation	Yield	ISO 527-2/50	5.0 %
		elongation	elongation	Yield4	ASTM D638	5.0 %
tensile strength	Break	ISO 527-2/50	40.0 Mpa
	tensile strength	Break4	ASTM D638	52.0 Mpa
		tensile strength	Yield	ISO 527-2/50	58.0 Mpa
		tensile strength	tensile strength	Yield4	ASTM D638	58.0 Mpa
Tensile modulus	--	ISO 527-2/1	2800 Mpa
Tensile modulus	Tensile modulus	--3	ASTM D638	2820 Mpa
Bending modulus	--6	ISO 178	2600 Mpa
bending strength	--6,7	ISO 178	90.0 Mpa
bending strength	bending strength	Yield, 50.0 mm Span5	ASTM D790	101 Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	Internal Method	19.0 mg

injection	Test Condition	Test Method	Test Result
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 80 %
Temperature at the rear of the barrel			230 to 250 °C
Temperature in the middle of the barrel			240 to 255 °C
Temperature at the front of the material cylinder			245 to 260 °C
Spray nozzle temperature			240 to 255 °C
Screw speed			50 to 100 rpm
Exhaust hole depth			0.013 to 0.025 mm
Processing (melt) temperature			245 to 260 °C
Mold temperature			50 to 75 °C
Back pressure			0.300 to 0.700 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	162 °C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span10	ISO 75-2/Be	150 °C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	74.0 °C
			Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	71.0 °C
				Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span10	ISO 75-2/Ae	60.0 °C
				Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	73.0 °C
Vicat softening temperature	--	ASTM D152511	170 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	212 °C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.9E-5 cm/cm/°C
thermal conductivity		ISO 8302	0.24 W/m/K
Linear coefficient of thermal expansion	Flow : 60 to 138°C	ASTM E831	1.3E-4 cm/cm/°C
	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ISO 11359-2	7.6E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Flow : 23 to 60°C	ISO 11359-2	1.0E-4 cm/cm/°C
			Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.9E-5 cm/cm/°C
				Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	7.3E-5 cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 60°C	ISO 11359-2	1.0E-4 cm/cm/°C
RTI Elec		UL 746	120 °C
RTI Imp		UL 746	120 °C
RTI		UL 746	140 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.080 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.36 %
Shrinkage rate	Across FlowFlow : 2.30 to 4.60 mm	Internal Method	1.6 - 2.4 %
	Shrinkage rate	Across FlowFlow : 0.750 to 2.30 mm	Internal Method	1.0 - 1.7 %
		Shrinkage rate	Across FlowFlow 2	Internal Method	0.90 - 1.9 %
			Shrinkage rate	Flow : 2.30 to 4.60 mm	Internal Method	1.5 - 2.3 %
				Shrinkage rate	Flow : 3.20 mm	Internal Method	1.5 - 2.3 %
					Shrinkage rate	Flow : 0.750 to 2.30 mm	Internal Method	0.90 - 1.6 %
					Shrinkage rate	Shrinkage rate	Flow 2	Internal Method	1.1 - 1.8 %
Melt Volume Flow Rate (MVR)	250°C/2.16 kg	ISO 1133	8.00 cm3/10min
melt mass-flow rate	250°C/2.16 kg	ASTM D1238	8.6 g/10 min
Specific volume		ASTM D792	0.710 cm³/g

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	1 MHz	IEC 60250	0.013
Hot wire ignition		UL 746	PLC 2
Surface resistivity		IEC 60093	> 1.0E+15 ohms
Volume resistivity		IEC 60093	> 1.0E+15 ohms·cm
Dielectric strength	1.60 mm, in Oil	ASTM D149	24 KV/mm
	Dielectric strength	3.20 mm, in Air	ASTM D149	18 KV/mm
		Dielectric strength	0.800 mm, in Oil	IEC 60243-1	35 KV/mm
			Dielectric strength	1.00 mm12	IEC 60243-1	18 KV/mm
				Dielectric strength	1.60 mm, in Oil	IEC 60243-1	25 KV/mm
				Dielectric strength	Dielectric strength	3.20 mm, in Oil	IEC 60243-1	17 KV/mm
Relative permittivity	50 Hz	IEC 60250	2.90
	Relative permittivity	60 Hz	IEC 60250	2.90
		Relative permittivity	100 Hz	IEC 60250	3.10
		Relative permittivity	Relative permittivity	1 MHz	IEC 60250	2.80
Dissipation factor	50 Hz	IEC 60250	1.0E-3
	Dissipation factor	60 Hz	IEC 60250	1.0E-3
	Dissipation factor	Dissipation factor	100 Hz	IEC 60250	2.0E-3
Arc resistance		ASTM D495	PLC 6
Compared to the anti leakage trace index		UL 746	PLC 3
Compared to the anti leakage trace index	Compared to the anti leakage trace index	--	IEC 60112	PLC 3
High voltage arc tracing rate		UL 746	PLC 4
Compared to the anti leakage trace index	Solution B	IEC 60112	PLC 4
High arc combustion index		UL 746	PLC 0
High Voltage Arc Resistance Index (HVAR) (PLC)		UL 746	PLC 6

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H 358/30	ISO 2039-1	105 Mpa
Rockwell hardness	R -Sale	ISO 2039-2	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.