Material Description
- Material Properties:Low liquidity
- Application Areas:Automotive Applications｜sporting goods
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.60 % | |
| 内部方法 | 0.20 % | ||
| Water absorption rate | ISO 62 | 0.020 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 123 |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 流动性.低光泽 | ||
| Color | 黑色 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| BarFlowLength | 内部方法 | 110 mm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2 | 155 Mpa | |
| Tensile strain | ISO 527-2 | 1.0 % | |
| Flexural modulus | ISO 178 | 20000 Mpa | |
| bending strength | ISO 178 | 245 Mpa | |
| shear strength | JISK7214 | 60.0 Mpa | |
| coefficient of friction | 0.30 | ||
| Taber abraser | ISO 9352 | 70.0 mg | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 9 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 22 kg·cm/cm(J/M)ft·lb/in | ||
| elongation at break | ASTM D638/ISO 527 | 1 % | |
| tensile strength | ASTM D638/ISO 527 | 95 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 123 | |
| Flexural modulus | ASTM D790/ISO 178 | 20 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 245 kg/cm²(MPa)[Lb/in²] |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 22 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| dielectric strength | IEC 60243-1 | 22 KV/mm | |
| dielectric constant | IEC 60250 | 4.90 | |
| Dissipation Factor | IEC 60250 | 2E-03 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.96 | |
| Shrinkage rate | ASTM D955 | 0.2 % | |
| Water absorption rate | ASTM D570/ISO 62 | 0.02 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 260 °C | |
| melting temperature | ISO 11357-3 | 278 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.8E-05 cm/cm/°C | |
| ISO 11359-2 | 2.7E-05 cm/cm/°C | ||
| Combustibility (rate) | UL 94 | V-0 | |
| Heat distortion temperature | ASTM D648/ISO 75 | >260 ℃（℉） | |
| melting temperature | 278 ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1.8 mm/mm.℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.