Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS A610MG1 TORAY JAPAN
Torelina®
Automotive Applications,sporting goods
Low liquidity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/A610MG1 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 22 kJ/m² |
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/A610MG1 |
|---|---|---|---|
| BarFlowLength | 320°C,1.00mm | 内部方法 | 110 mm |
| hardness | Test Condition | Test Method | TORAY JAPAN/A610MG1 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 123 |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/A610MG1 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 245 kg/cm²(MPa)[Lb/in²] | |
| shear strength | 23°C | JISK7214 | 60.0 Mpa |
| Flexural modulus | ASTM D790/ISO 178 | 20 kg/cm²(MPa)[Lb/in²] | |
| coefficient of friction | 0.30 | ||
| Taber abraser | 1000Cycles | ISO 9352 | 70.0 mg |
| elongation at break | ASTM D638/ISO 527 | 1 % | |
| Rockwell hardness | ASTM D785 | 123 | |
| tensile strength | ASTM D638/ISO 527 | 95 kg/cm²(MPa)[Lb/in²] | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 1.0 % |
| bending strength | 23°C | ISO 178 | 245 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 155 Mpa |
| Flexural modulus | 23°C | ISO 178 | 20000 Mpa |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 22 kg·cm/cm(J/M)ft·lb/in |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/A610MG1 |
|---|---|---|---|
| dielectric constant | 23°C,1MHz | IEC 60250 | 4.90 |
| dielectric strength | IEC 60243-1 | 22 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 2E-03 |
| other | Test Condition | Test Method | TORAY JAPAN/A610MG1 |
|---|---|---|---|
| characteristic | 流动性.低光泽 | ||
| Color | 黑色 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/A610MG1 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.2 % | |
| density | ASTM D792/ISO 1183 | 1.96 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.02 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/A610MG1 |
|---|---|---|---|
| UL flame retardant rating | 0.73mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TORAY JAPAN/A610MG1 |
|---|---|---|---|
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 0.60 % |
| MD:3.00mm4 | 内部方法 | 0.20 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.020 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/A610MG1 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 278 °C | |
| Combustibility (rate) | UL 94 | V-0 | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | >260 ℃（℉） |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 260 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.8E-05 cm/cm/°C |
| melting temperature | 278 ℃（℉） | ||
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 2.7E-05 cm/cm/°C |
| ASTM D696/ISO 11359 | 1.8 mm/mm.℃ |